BASF Ultramid® B3S HP PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3S HP PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3S HP is a easy flowing, finely crystalline, injection molding PA6 for fast processing
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 9.0 - 10 % | 9.0 - 10 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.6 - 3.4 % | 2.6 - 3.4 % | (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 145 cm³/g | 145 cm³/g | Viscosity number; ISO 307 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 198 g/10 min @Load 5.00 kg, Temperature 275 °C |
198 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 20 % | 20 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 1.20 GPa | 174 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 180/A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 1100 MPa @Strain 0.500 % |
160000 psi @Strain 0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 87.0 °C | 189 °F | for 50% loss of tensile strength after 20,000 hr |
| 97.0 °C | 207 °F | for 50% loss of tensile strength after 5,000 hr | |
| 180 °C | 356 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 7.0 @Frequency 1.00e+6 Hz |
7.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.30 @Frequency 1.00e+6 Hz |
0.30 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | RG-NAFTA | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Reliance Industries Relene F46003 Polyethylene
- Materion Beryllium Copper Alloy 25 Wire; 1/4H (TD01) Temper; 1.3-12.7 mm Diameter (UNS C17200)
- Michelman® Michem® Emulsion 48040M2 Nonionic microcrystalline wax emulsion
- Lucas-Milhaupt Dry Flux Silver Brazing Flux
- SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Asia Pacific)
- SABIC Innovative Plastics Valox® IQ357M PBT+PC (Asia Pacific)
- SABIC Innovative Plastics LNP STAT-KON MD000I PP (Europe-Africa-Middle East)
- Hexcel® HexWeb® CR-PAA™ 5/32-5056-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb
- 3M Controltac™ 3545C Removable Graphic Film with Comply™ Adhesive
- Resinlab® EP1026R Rubber Modified Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved