Asahi Kasei Leona® 1700S Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Asahi Kasei |
| Trade Name | Leona® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Leona® 1700S Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Similar to 1500 but with even higher molecular weight. Suitable for extrusion of thick-wall parts.Applications:Rods, films Information provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | Dry; ASTM D792 |
| Water Absorption | 2.5 % | 2.5 % | Wet |
| Linear Mold Shrinkage | 0.013 - 0.020 cm/cm | 0.013 - 0.020 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 55 | 55 | Wet; ASTM D785 |
| 80 | 80 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 105 | 105 | Wet; ASTM D785 |
| 120 | 120 | Dry; ASTM D785 | |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Wet; ASTM D638 |
| 80.0 MPa | 11600 psi | Dry; ASTM D638 | |
| Elongation at Break | 100 % | 100 % | Dry; ASTM D638 |
| 300 % | 300 % | Wet; ASTM D638 | |
| Flexural Strength | 54.0 MPa | 7830 psi | Wet; ASTM D790 |
| 118 MPa | 17100 psi | Dry; ASTM D790 | |
| Flexural Modulus | 1.20 GPa | 174 ksi | Wet; ASTM D790 |
| 2.80 GPa | 406 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | Dry; ASTM D256 |
| 2.45 J/cm | 4.59 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 4.0 | 4.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
Dry; ASTM D696 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | Dry |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | Dry |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Dry; ASTM D648 |
| Oxygen Index | 23 % | 23 % | Dry; ASTM D2863 |
Users viewing this material also viewed the following:
- Poco Graphite PLS Semiconductor Grade Graphite
- PTS Tristar® PC-10FR-(VIK) 16 MFI Flame Retardant, UV Stabilized Polycarbonate With Impact Modifier and Release
- Materion Beryllium Copper Alloy 10 Wire; H (TD04) Temper; 1.3-12.7 mm Diameter (UNS C17500)
- Indium Corp. Indalloy 90 Indium Solder Alloy
- Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA), 65% GlassMineral (Conditioned)
- A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene
- BASF Isopropylamine
- Aremco Aremco-Bond™ 526N High Performance Epoxide
- Dow LDPE 535I Low Density Polyethylene, Liner Grade
Copyright © lookpolymers.com All Rights Reserved