Asahi Kasei Leona® 13G43 43% Glass Filled Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Asahi Kasei
Trade Name Leona®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asahi Kasei Leona® 13G43 43% Glass Filled Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
43% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Mechanical and electrical parts such as micromotors, automotive parts such as radiator tanks and shift leversInformation provided by Asahi Kasei
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
Dry; ASTM D792
Water Absorption 1.4 %
1.4 %
Wet
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Dry; ASTM D2863
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
Dry; ASTM D2863
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80
80
Wet; ASTM D785
96
96
Dry; ASTM D785
Hardness, Rockwell R 118
118
Dry; ASTM D785
Tensile Strength, Yield 157 MPa
22800 psi
Wet; ASTM D638
196 MPa
28400 psi
Dry; ASTM D638
Elongation at Break 3.0 %
3.0 %
Dry; ASTM D638
4.0 %
4.0 %
Wet; ASTM D638
Flexural Strength 235 MPa
34100 psi
Wet; ASTM D790
314 MPa
45500 psi
Dry; ASTM D790
Flexural Modulus 8.30 GPa
1200 ksi
Wet; ASTM D790
11.8 GPa
1710 ksi
Dry; ASTM D790
Izod Impact, Notched 1.27 J/cm
2.38 ft-lb/in
Dry; ASTM D256
2.06 J/cm
3.86 ft-lb/in
Wet; ASTM D256
Taber Abrasion, mg/1000 Cycles 19
19
Wet; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear 30.0 µm/m-°C

@Temperature 20.0 °C
16.7 µin/in-°F

@Temperature 68.0 °F
Dry; ASTM D696
Thermal Conductivity 0.400 W/m-K
2.78 BTU-in/hr-ft²-°F
Dry
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Dry; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Dry; ASTM D648
Flammability, UL94 HB
HB
Dry