Nilit FRIANYL B63 TF20 Nylon 6 for injection molding, 20% PTFE lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, PTFE Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 TF20 Nylon 6 for injection molding, 20% PTFE lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 6.0 % | 5.0 - 6.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.015 cm/cm | 0.0080 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 115 MPa | 16700 psi | ISO 2039-1 |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB | NB | DIN 53453 | |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| 0.900 J/cm² | 4.28 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 500 V | 500 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Polykemi AB POLYlux 3809S PC/PBT-Blend
- Stir SpA C 2053 68 AT (PVC)
- Solvay TECHNYL® A 118L V50 PA66, 50% glass fiber, Eh 0
- Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Conditioned
- Total PPH 3270 Polypropylene Homopolymer, High Crystallinity, Low Melt Flow Film Grade
- ChevronTexaco TEGRA® ISO 68 Synthetic Compressor Oil
- Addcomp ADD-VANCE® THC 831 PP based masterbatch containing heat stabilizers, coupling agent and carbon black
- Arkema Group Rilsan® 8020 Nylon 11, Flexible Tubing Grade (Conditioned)
- SABIC Innovative Plastics Lexan® FR65 Polycarbonate Film, Flame Retardant
- Overview of materials for Polypropylene with 30% Glass Fiber Filler
Copyright © lookpolymers.com All Rights Reserved