Kennametal Stellite Nistelle® C-4C Nickel Alloy
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Kennametal Stellite |
| Trade Name | Nistelle® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kennametal Stellite Nistelle® C-4C Nickel Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Comparable to Tribaloy Alloy 745. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 238 | 238 | Converted from Rockwell C hardness. |
| Hardness, Knoop | 279 | 279 | Converted from Rockwell C hardness. |
| Hardness, Rockwell A | 61 | 61 | Converted from Rockwell C hardness. |
| Hardness, Rockwell B | 100 | 100 | Converted from Rockwell C hardness. |
| Hardness, Rockwell C | 17 - 27 | 17 - 27 | |
| Hardness, Vickers | 245 | 245 | Converted from Rockwell C hardness. |
| Tensile Strength, Ultimate | 793 MPa | 115000 psi | |
| Elongation at Break | 25 % | 25 % |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.050 % | <= 0.050 % | |
| Chromium, Cr | 17 % | 17 % | |
| Iron, Fe | <= 2.0 % | <= 2.0 % | |
| Molybdenum, Mo | 16 % | 16 % | |
| Nickel, Ni | 63.5 % | 63.5 % | As Remainder |
| Silicon, Si | <= 1.5 % | <= 1.5 % |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 66-13GF 13% Glass Fiber Filled Nylon 66 for Injection Molding
- Pacific Sintered Materials FS-1601 Silicon Iron Soft Magnetic Powdered Metal
- DuPont Elvax® CE9616-1 Ethylene Vinyl Acetate (discontinued **)
- LATI Latamid 66 E21 PA 66, Impact Modified
- Ineos L24G-00 Polypropylene Impact Copolymer
- Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet
- Covestro Desmopan® 150 Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved