Arlon 49586B010 0.0115" (0.292 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 49586B010 0.0115" (0.292 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 1681 FiberglassSide 2: Uncured Silicone RubberInterleave: Polyethylene This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.34 g/cc	0.0484 lb/in³	Side 2, Silicone Property; Arlon SQA-TMS-024
	1.56 g/cc	0.0564 lb/in³	Side 1, Silicone Property; Arlon SQA-TMS-024
Thickness	50.8 microns	2.00 mil	Side 1; Arlon SQA-TMS-003
	76.2 microns	3.00 mil	Interleave
	102 microns	4.00 mil	Side 2; Arlon SQA-TMS-003
	140 microns	5.50 mil	Substrate; Arlon SQA-TMS-003
	292 microns	11.5 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	37	37	Side 2, Silicone Property; ASTM D2240
	55	55	Side 1, Silicone Property; ASTM D2240
Tensile Strength	3.65 MPa	530 psi	Side 1, Silicone Property; ASTM D412
	6.55 MPa	950 psi	Side 2, Silicone Property; ASTM D412
Elongation at Break	300 %	300 %	Side 1, Silicone Property; ASTM D412
	620 %	620 %	Side 2, Silicone Property; ASTM D412
Tear Strength	7.01 kN/m	40.0 pli	Side 1, Silicone Property; ASTM D624
	26.3 kN/m	150 pli	Side 2, Silicone Property; ASTM D624
Peel Strength	2.17 kN/m	12.4 pli	Bond Strength

Thermal Properties	Metric	English
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Dielectric Strength	35.4 kV/mm	900 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 350 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 21.1 °C	6.00 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Black
	Black	Substrate
Total Product Weight (oz/yd2)	12.7