- Arlon 19606R025 0.025" Uncured/Cured Silicone Rubber with Fiberglass Substrate
Arlon 19606R025 0.025" Uncured/Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 19606R025 0.025" Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Cured Silicone RubberSubstrate: Prime Coated 1523 FiberglassSide 2: Uncured Silicone RubberInterleave: 0.003" PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 102 microns | 4.00 mil | Side 1; Arlon SQA-TMS-003 |
| 178 microns | 7.00 mil | Side 2; Arlon SQA-TMS-003 | |
| 356 microns | 14.0 mil | Substrate; Arlon SQA-TMS-003 | |
| 635 microns | 25.0 mil | Overall Thickness; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | Silicone Property |
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property |
| Elongation at Break | 375 % | 375 % | Silicone Property |
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended post Cure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 21.1 °C |
6.00 Month @Temperature 70.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 27.1 | |
| Uncoated Fabric Break Strength (lb/in) | 300 | Fill Direction; Substrate Property |
| 450 | Warp Direction; Substrate Property |
Users viewing this material also viewed the following:
- Polykemi AB SCANMID 6 B11^ F50 Nylon 6, Glass Fiber Reinforced
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 1-D Heavy Oil Plasticizer
- NOVA Chemicals Novapol® TR-0535-UI Hexene MDPE Rotational Molding Resin
- Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F)
- Shamrock Technologies MicroFLON® 1433FG Thermoplastic Grade PTFE Additive
- Schott N-KZFS4 Glass
- Entec Hypro™ PPH-CC40 Natural Homopolymer Polypropylene, 40% Calcium Carbonate Filled
- Arlon 51576R015A 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- ITW Plexus Plexus™ MA340 Methacrylate Adhesive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Laminar Filler
Copyright © lookpolymers.com All Rights Reserved