Arkema Group Oroglas® VS-UVT Acrylic, Injection Molding Grade  (discontinued **)

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Oroglas® VS-UVT Acrylic, Injection Molding Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The outstanding flow of OROGLAS VS-UVT makes it as the material of choice for injection molding of part with thin wall thickness.The ultraviolet transmitting ( uvt) formulation is developed to meet the specific requirement of medical diagnostic components.OROGLAS VS-UVT is FDA approved.ISO data provided by the manufacturer, Arkema.Arkema, formed in 2004, was formerly Atofina Chemicals and before that Elf Atochem.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Water Absorption 1.7 %
1.7 %
Moisture Absorption at Equilibrium 0.30 %
0.30 %
Humidity Absorption
Melt Flow 22 g/10 min

@Load 3.80 kg,
Temperature 230 °C
22 g/10 min

@Load 8.38 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min
Elongation at Break 5.0 %
5.0 %
Nominal Strain; 50 mm/min
Tensile Modulus 2.90 GPa
421 ksi
1 mm/min
Charpy Impact Unnotched 1.90 J/cm²
9.04 ft-lb/in²
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
Tensile Creep Modulus, 1 hour 2400 MPa
348000 psi
Tensile Creep Modulus, 1000 hours 1400 MPa
203000 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
Vicat Softening Point 80.0 °C
176 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Optical Properties Metric English Comments
Transmission, Visible 80 %
80 %
Mfr. reports 'Transparent' but doesn't quantify.
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 3.2

@Frequency 1e+6 Hz
3.2

@Frequency 1e+6 Hz
3.7

@Frequency 100 Hz
3.7

@Frequency 100 Hz
Dielectric Strength 19.7 kV/mm
500 kV/in
Dissipation Factor 0.040

@Frequency 1e+6 Hz
0.040

@Frequency 1e+6 Hz
0.050

@Frequency 100 Hz
0.050

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V