Arlon R36319R028 Silicone Rubber/Fiberglass Laminate
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon R36319R028 Silicone Rubber/Fiberglass Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Interleave: 3 mil PE; Layer 2: uncured silicone rubber; Layer 1: Cured silicone rubber; Substrate: 162 fiberglass
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | Arlon SQA-TMS-024 |
| Thickness | 127 microns | 5.00 mil | layer 1; Arlon SQA-TMS-003 |
| 152 microns | 6.00 mil | layer 2; Arlon SQA-TMS-003 | |
| 432 microns | 17.0 mil | substrate; Arlon SQA-TMS-003 | |
| 711 microns | 28.0 mil | overall; Arlon SQA-TMS-003 | |
| Outgassing - Total Mass Loss | 0.34 % | 0.34 % | post cured; ASTM E 595 |
| 1.07 % | 1.07 % | no post cure; ASTM E 595 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 48 | 48 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 5.86 MPa | 850 psi | ASTM D412 |
| Elongation at Break | 450 % | 450 % | silicone property; ASTM D412 |
| Adhesive Bond Strength | 0.103 MPa | 15.0 psi | Arlon SQA-TMS-047 |
| Tear Strength | 12.3 kN/m | 70.0 pli | Die B; silicone property; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 14.4 kV/mm | 365 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 218 °C |
2.00 hour @Temperature 425 °F |
|
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
||
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Outgassing - CVCM (%) ASTM E595 | 0.1 | post cured |
| 0.28 | no post cure |
Users viewing this material also viewed the following:
- Nanocyl EPOCYL™ NC E128-02 Master Batch Liquid Bisphenol-A Resin for non-Solvent Based Formulation Purposes
- PTS Trimid® N6-G33L 33% GFR Lubricated Nylon 6
- Techmer ES Electrablend® ABS SS5 5% Stainless Steel Filled
- SABIC Innovative Plastics LNP VERTON RV007E PA 66 (Europe-Africa-Middle East)
- Unitika RUN35-C25 PA6, Dry
- EMS-Griltech Griltex® D 1502E Copolyester Hotmelt Adhesive (Technical Applications)
- CMW® ELKONITE® 50W3 Tungsten Copper material ASTM B702
- Arkema Group Rilsan® KMVO 39099 TL Nylon 11 (Conditioned)
- ConocoPhillips Conoco® El Mar® Ashless Supreme Oil, SAE Viscosity Grade 40
Copyright © lookpolymers.com All Rights Reserved