- A. Schulman ComAlloy Hiloy® 261 Glass Reinforced, Modified SMA
A. Schulman ComAlloy Hiloy® 261 Glass Reinforced, Modified SMA
| Category | Polymer , Thermoplastic , SMA Polymer , Glass Reinforced, Modified SMA |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 261 Glass Reinforced, Modified SMA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.10% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 63.0 MPa | 9140 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 246 - 266 °C | 475 - 511 °F |
Users viewing this material also viewed the following:
- Permabond LH054 Anaerobic Threadsealant
- Manifattura Cattaneo PA 6.6 30% GF Nylon, Glass Filled
- Ferro IP 510 Thick Film Glass
- A. Schulman POLYBATCH™ Green P30244/4 Concentrate Based In Copolymer PP
- Eagle Brass 70265 XP175, Hard
- ExxonMobil Nexxstar™ NX-00328 Low Density Polyethylene Resin
- Dow Corning 2-0400 DIMETHYLCHLOROSILANE (ME2HSICL) DIST
- Ascend Performance Materials Vydyne® R533 NT Nylon 66, 33% Glass Reinforced, DAM
- Arlon R31551R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate
- DuPont Elvax® 3130SBZ Ethylene-Vinyl Acetate Copolymer Resin for Blown Film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved