Arkema Group Orgalloy® LT 5050 ES Polyamide Alloy

Category Polymer , Thermoplastic , Nylon
Manufacturer Arkema
Trade Name Orgalloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® LT 5050 ES Polyamide Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO R1183
Water Absorption 1.35 %
1.35 %
23°C / 24 hrs; ISO 62
Melt Flow 0.50 g/10 min

@Load 5.00 kg,
Temperature 235 °C
 0.50 g/10 min

@Load 11.0 lb,
Temperature 455 °F
 after drying; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 55
55
ISO 868
Tensile Strength, Ultimate 35.0 MPa
5080 psi
ISO R527
Tensile Strength, Yield 23.0 MPa
3340 psi
ISO R527
Elongation at Break 260 %
260 %
ISO R527
Elongation at Yield 3.5 %
3.5 %
ISO R527
Modulus of Elasticity 0.460 GPa
66.7 ksi
ISO R527
Flexural Modulus 0.500 GPa
72.5 ksi
After conditioning at 23°C and 50% RH; ISO 178
0.800 GPa
116 ksi
Dry; ISO 178
Charpy Impact, Notched NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
 ISO 179/Af
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/Af
Tensile Creep Modulus, 1 hour 420 MPa
60900 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear 170 µm/m-°C

@Temperature 20.0 - 60.0 °C
 94.4 µin/in-°F

@Temperature 68.0 - 140 °F
 TMS2 Perkin Elmer
CTE, linear, Transverse to Flow 180 µm/m-°C

@Temperature 20.0 - 60.0 °C
 100 µin/in-°F

@Temperature 68.0 - 140 °F
 TMS2 Perkin Elmer
Melting Point 220 °C
428 °F
ISO R1218
Vicat Softening Point 198 °C
388 °F
10 N - A method; ISO 306
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 7.40e+13 ohm-cm
7.40e+13 ohm-cm
ASTM D257
Surface Resistance 3.10e+15 ohm
3.10e+15 ohm
ASTM D257
Dielectric Strength 36.0 kV/mm

@Thickness 1.00 mm
 914 kV/in

@Thickness 0.0394 in
 ASTM D149
Dissipation Factor 0.050

@Frequency 100000 Hz
 0.050

@Frequency 100000 Hz
 NFC 26 230
0.11

@Frequency 100 Hz
 0.11

@Frequency 100 Hz
 NFC 26 230
0.11

@Frequency 1000 Hz
 0.11

@Frequency 1000 Hz
 NFC 26 230
Comparative Tracking Index >= 600 V
>= 600 V
NFC 26 220