- Aremco Aremco-Bond™ 2318 High Performance Epoxide
Aremco Aremco-Bond™ 2318 High Performance Epoxide
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 2318 High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | |
| Viscosity | 16000 cP | 16000 cP | mixed viscosity |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 89 | 89 | |
| Flexural Strength | 97.2 MPa | 14100 psi | ASTM D790 |
| Shear Strength | 7.826 MPa | 1135 psi | ASTM D1002-94 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.2 µm/m-°C | 39.0 µin/in-°F | |
| Thermal Conductivity | 0.634 W/m-K | 4.40 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | |
| Dielectric Constant | 4.8 @Frequency 1000 Hz |
4.8 @Frequency 1000 Hz |
|
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | |
| Dissipation Factor | 0.014 | 0.014 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
recommended cure |
| 240 min @Temperature 20.0 °C |
4.00 hour @Temperature 68.0 °F |
recommended cure | |
| 1440 - 2880 min @Temperature 23.0 °C |
24.0 - 48.0 hour @Temperature 73.4 °F |
||
| Pot Life | 42.0 min @Temperature 25.0 °C |
42.0 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Excellent | |
| Color | Black | |
| Mix Ratio | 100:12 |
Users viewing this material also viewed the following:
- KYDEX® V103 High Impact Fire-Rated Thermoforming Sheet
- Lehmann & Voss LUVOCOM® 1105-0950/RD PEEK, unreinforced
- Lanxess Durethan® DP BKV 60 EF 000000 Nylon6, 60% Glass Fiber
- SABIC Innovative Plastics LNP LUBRILOY RF206H PA 66 (Asia Pacific)
- A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
- EMS-Griltech Grilon® XA 893 Nylon 6 Monofilament (Super-Set)
- ExxonMobil LDPE LD 100BW Low Density Polyethylene Resin
- Colorite Polymers 7011 Clear Extrusion Vinyl Compound
- Resinlab® EP1285HD-14 Highly Filled, Medium Viscosity Casting Resin
Copyright © lookpolymers.com All Rights Reserved