- Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Longitudinal Properties
Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Longitudinal Properties
| Category | Metal , Ferrous Metal , Stainless Steel |
| Manufacturer | Carpenter Technology Corporation (Cartech) |
| Trade Name | Pyrowear® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Longitudinal Properties.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Carpenter Technology Corporation.This is a carburizing, corrosion resistant steel designed to provide a case hardness in excess of HRC 60 combined with a tough, ductile core. The corrosion resistance of carburized Pyrowear® 675 stainless is similar to that of Type 440C stainless, while the core toughness is similar to that of AISI 9310. In addition, the alloy provides excellent hot hardness capability. This alloy has been used in bearing and gear type applications.Pyrowear® is a registered trademark of Carpenter Technology Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.756 g/cc | 0.2802 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 379 | 379 | Estimated from Rockwell C for 3000 kg load, 10 mm ball Brinell measurement. |
| Hardness, Knoop | 414 | 414 | Estimated from Rockwell C |
| Hardness, Rockwell C | 41 | 41 | |
| Hardness, Vickers | 396 | 396 | Estimated from Rockwell C |
| Tensile Strength, Ultimate | 1276 MPa | 185100 psi | |
| Tensile Strength, Yield | 1062 MPa @Strain 0.200 % |
154000 psi @Strain 0.200 % |
|
| Elongation at Break | 20 % | 20 % | In 4D |
| Reduction of Area | 75 % | 75 % | |
| Modulus of Elasticity | 204 GPa | 29600 ksi | |
| Fracture Toughness | 138 MPa-m½ | 126 ksi-in½ | K(Q) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.01 µm/m-°C @Temperature 25.0 - 93.0 °C |
5.561 µin/in-°F @Temperature 77.0 - 199 °F |
|
| 10.62 µm/m-°C @Temperature 25.0 - 260 °C |
5.900 µin/in-°F @Temperature 77.0 - 500 °F |
||
| 11.56 µm/m-°C @Temperature 25.0 - 538 °C |
6.422 µin/in-°F @Temperature 77.0 - 1000 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.070 % | 0.070 % | |
| Chromium, Cr | 13 % | 13 % | |
| Cobalt, Co | 5.4 % | 5.4 % | |
| Iron, Fe | 76 % | 76 % | as remainder |
| Manganese, Mn | 0.65 % | 0.65 % | |
| Molybdenum, Mo | 1.8 % | 1.8 % | |
| Nickel, Ni | 2.6 % | 2.6 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Vanadium, V | 0.60 % | 0.60 % |
Users viewing this material also viewed the following:
- Nylene® Naxel™ PC524 Flame Retardant Polycarbonate
- PolyOne Edgetek® 5209 Natural 1 Acetal (POM) Copolymer
- KYDEX® XD MB 3D Laminate Thermoplastic 3D Laminate for Flat Lamination and Membrane Pressed Uses with Microban®
- Taiwan PU Corporation TPU-C75 General Grade, Calender Molding Polyester Base TPU
- Shandong Rike Chemical HELIâ„¢ HL-275S PVC Processing Aid Series (PA)
- Saint-Gobain Norton® Fluorglas® Chemfilm® R167 Extruded Expanded PTFE Film (0.006" thick)
- Tisan TISLAMID® 6 UNR Nylon 6
- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
- Hexcel® HexWeb® CR III 3/8-5052-.005 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Bhansali Engineering Abstron IM-11B ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved