Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic |
Manufacturer | Amity Thermosets |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Amity Thermosets ATM 122 Phenolic Molding Organic Filler, Compression Molded.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.38 - 1.41 g/cc | 0.0499 - 0.0509 lb/in³ | Molding; IS 867-1963 |
Apparent Bulk Density | 0.620 - 0.680 g/cc | 0.0224 - 0.0246 lb/in³ | IS 867-1963 |
Water Absorption | 0.40 - 0.60 % | 0.40 - 0.60 % | IS 13411-1993 |
Linear Mold Shrinkage | 0.0070 - 0.0086 cm/cm | 0.0070 - 0.0086 in/in | IS 13411-1992 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 46.0 - 60.0 MPa | 6670 - 8700 psi | 5 mm/min.; IS 867-1963 |
Shear Strength | 64.0 - 74.0 MPa | 9280 - 10700 psi | 2mm/min.; IS 867-1963 |
Izod Impact, Notched | 0.280 - 0.420 J/cm | 0.525 - 0.787 ft-lb/in | IS 13411-1992 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 3.2e+10 - 3.2e+11 ohm-cm | 3.2e+10 - 3.2e+11 ohm-cm | IS 3396-1979 |
Surface Resistance | 3.2e+9 - 3.2e+10 ohm | 3.2e+9 - 3.2e+10 ohm | IS 3396-1979 |
Dielectric Strength | 5.00 - 7.00 kV/mm @Temperature 90.0 °C |
127 - 178 kV/in @Temperature 194 °F |
IS 2584-1963 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
Cure Time | 0.333 - 0.417 min | 0.00556 - 0.00694 hour | per mm |
Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |