- Addiplast Addinyl PMD 20117 Flame Retardant Nylon, Glass Filled
Addiplast Addinyl PMD 20117 Flame Retardant Nylon, Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl PMD 20117 Flame Retardant Nylon, Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, glass fiver reinforced, friction resistantInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | Conditioned; ISO 868 |
| 84 | 84 | ISO 868 | |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned; ISO R 527 |
| 110 MPa | 16000 psi | ISO R 527 | |
| Elongation at Break | 4.0 % | 4.0 % | ISO R 527 |
| 5.0 % | 5.0 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 5.00 GPa | 725 ksi | Conditioned; ISO 178 |
| 8.00 GPa | 1160 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180/1A |
| 7.00 kJ/m² | 3.33 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/IeU |
| 4.00 J/cm² | 19.0 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/IeA |
| 0.750 J/cm² | 3.57 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-2/AF |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | Conditioned; CEI 60093 |
| 1.00e+13 ohm | 1.00e+13 ohm | CEI 60093 | |
| Comparative Tracking Index | 300 V | 300 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 20 GB 10 PA6, 20% glass fibre, 10% glass beads
- NanoAmor 90%, OD: 1-2 nm OH Functionalized Single-Walled Carbon Nanotubes
- Overview of materials for Polyester Thermoplastic Elastomer
- ExxonMobil LL 6100 Injection Molding Resin (discontinued **)
- Sylvin Technologies 9915-95 Natural PVC Molding Compound
- Saint-Gobain CHR® SG35-06(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Loctite® 3440 1 component Gold/polymer filler Anisotropic Epoxy Adhesive
- Dow Corning Z-6341 SILANE
- ExxonMobil Solvesso™ 150 Aromatic Fluid
- ATI Allegheny Ludlum T-436 Ferritic Stainless Steel, UNS S43600
Copyright © lookpolymers.com All Rights Reserved