Addiplast Addinyl A2 1 Flame Retardant Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl A2 1 Flame Retardant Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, halogen freeInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 78 | 78 | Conditioned; ISO 868 |
| 85 | 85 | ISO 868 | |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Conditioned; ISO R 527 |
| 60.0 MPa | 8700 psi | ISO R 527 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO R 527 |
| 15 % | 15 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | Conditioned; ISO 178 |
| 3.50 GPa | 508 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A |
| 8.00 kJ/m² | 3.81 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/IeU |
| NB | NB | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | ISO 179/IeA |
| 0.700 J/cm² | 3.33 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-2/AF |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| Oxygen Index | 38 % | 38 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | Conditioned; CEI 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | CEI 60093 | |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | CEI 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ 5010UV Polyolefin
- Resin Technology Group TIGA 901 Room Temperature Curing Silver Conductive Epoxy
- SGL Carbon Group EK 2230 Carbon Graphite
- SABIC Innovative Plastics LNP THERMOCOMP PF008 PA 6
- SABIC Innovative Plastics LNP THERMOCOMP UF0067W PPA
- SABIC Innovative Plastics Xenoy® XD1507S PBT+PC (Europe-Africa-Middle East)
- Borealis LE0315-99 Polyethylene Thermoplastic Semiconductive Compound
- Polyram PlusTek RA304G6 Nylon 6.6, 30% Glass Fiber
- Parker Chomerics Waveguide Gaskets 873 Conductive Silicone Elastomer Gasket
Copyright © lookpolymers.com All Rights Reserved