Aclo Accutech Polypropylene Homopolymer HP0339W20L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339W20L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 19 % | 19 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.299 GPa | 333.5 ksi | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C | 154 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 505R PC (Europe-Africa-Middle East)
- Chase Plastics CP Pryme® N310L (Dry) Nylon 6, 10% Glass Fiber Reinforced, Lubricated, Recycled Content
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
- Wanhua Chemical Wanthane® WHT-1680AB Polyester Based TPU
- EMS-Grivory Grivory® HT2V-3X V0 nat 6059 PA6T/66-GF30
- Diamond Polymers ABS 3500ELG
- CMW® ELKONITE® 10W53 Heat Treatable Copper Tungsten
- Polyram RamOfin PPC361T4 Polypropylene, 20% Mineral Filled
- ChevronTexaco Hot Punch Compound H
- DuPont™ Clysar® ABL Polyolefin Shrink Packaging Film, 125 Gauge (discontinued **)
Copyright © lookpolymers.com All Rights Reserved