Aclo Accutech Polypropylene Homopolymer HP0339W20L Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339W20L Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D638 |
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 0.299 J/cm | 0.560 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C | 154 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion L0148 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Polymax® Maxelast® P3838 TPE, PP Overmold or Standalone use
- Parker Chomerics CHO-BOND 1067 Splicing Compound Kit
- Solvay Specialty Polymers Solef® 6008 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
- Lehmann & Voss LUVOCOM® 20-7314 Polyphthalamide, with PTFE
- A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT
- Tisan TISOPLEN® 10% Talc Filled Heat Stabilized Homopolymer Polypropylene
- 3M FV098 Soft Translucent Vinyl Label Products
- 3M 12054 Black 1/4" (6.4 mm) Polyurethane Foam
- Fainplast Compounds R 314 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved