Hexcel® HexWeb® HRH-327 - 3/16 - 5.0 Fiberglass Reinforced Polyimide Honeycomb

Category Other Engineering Material , Composite Fibers , Polymer , Thermoset , Polyimide, TS
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRH-327 - 3/16 - 5.0 Fiberglass Reinforced Polyimide Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size (inches)-DensityHexWeb® HRH-327 is a glass-fabric, bias weave reinforced plastic honeycomb that incorporates a polyimide resin system for the node adhesive as well as both the initial and final web impregnations. This material has been developed for extended service temperatures up to 500°F with short-term capabilities up to 700°F. Unless other specified, material will have standard postcure.Features: High-strength retention up to 500°F continuous service; 700°F short and intermittent term exposures; All polyimide resin and adhesive system; Good dielectric properties; Good insulative properties; Compatible with Hexcel polyimide adhesive, foam, and prepreg.Applications: A high-temperature nonmetallic honeycomb for use in sandwich structures that require good electrical properties or that see service temperatures in the range of 350°F-500°F. Applications include sandwich structures for Mach 2 and Mach 3 aircraft, high-energy radomes, structural and acoustical engine inlets and liners.
Physical Properties Metric English Comments
Density 0.0801 g/cc
0.00289 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 3.31 MPa
>= 480 psi
Stabilized, min, preliminary value obtained at .500 inch thickness
4.14 MPa
600 psi
Stabilized, typ, preliminary value obtained at .500 inch thickness
Compressive Modulus 0.469 GPa
68.0 ksi
Stabilized, typ, preliminary value obtained at .500 inch thickness
Shear Modulus 0.0827 GPa
12.0 ksi
Plate Shear, W Direction, typ, preliminary value obtained at .500 inch thickness
0.255 GPa
37.0 ksi
Plate Shear, L Direction, typ, preliminary value obtained at .500 inch thickness
Shear Strength >= 0.931 MPa
>= 135 psi
Plate Shear, W Direction, min, preliminary value obtained at .500 inch thickness
1.24 MPa
180 psi
Plate Shear, W Direction, typ, preliminary value obtained at .500 inch thickness
>= 1.93 MPa
>= 280 psi
Plate Shear, L Direction, min, preliminary value obtained at .500 inch thickness
2.55 MPa
370 psi
Plate Shear, L Direction, typ, preliminary value obtained at .500 inch thickness
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 260 °C
500 °F
Extended
371 °C
700 °F
Short Term