- Star Plastics PC/PBT7804 Molding Grade PC/PBT
Star Plastics PC/PBT7804 Molding Grade PC/PBT
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Star Plastics, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Star Plastics PC/PBT7804 Molding Grade PC/PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Star Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | ASTM D638 |
| Tensile Modulus | 1.86 GPa | 270 ksi | ASTM D638 |
| Flexural Yield Strength | 72.4 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 1.97 GPa | 285 ksi | ASTM D790 |
| Izod Impact, Notched | 6.67 J/cm | 12.5 ft-lb/in | 73°F, 0.125 in.; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | unannealed, .125in; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 249 °C | 450 - 480 °F | |
| Middle Barrel Temperature | 246 - 260 °C | 475 - 500 °F | |
| Front Barrel Temperature | 246 - 266 °C | 475 - 510 °F | |
| Nozzle Temperature | 252 - 266 °C | 485 - 510 °F | |
| Melt Temperature | 252 - 274 °C | 485 - 525 °F | |
| Mold Temperature | 48.9 - 87.8 °C | 120 - 190 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Screw Speed | 40 - 75 rpm | 40 - 75 rpm |
Users viewing this material also viewed the following:
- PolyOne Dynalloy™ 8900-30 Thermoplastic Elastomer (TPE)
- ExxonMobil Escorene® LD-409 EVA for Low Voltage Insulation (discontinued **)
- Idemitsu Kosan Xarec® WA 204 SPS, 20% Glass Filled
- Teknor Apex Monprene® MP-2825E Thermoplastic Elastomer
- A. Schulman POLYBLAK™ 3422 Black Color Concentrate, 35% Carbon Black Based In LDPE
- ExxonMobil LLDPE LL 6100.17 Linear Low Density Polyethylene Resin
- ATG s.r.l. IIR Butyl Rubber
- Asahi Kasei Thermylene® P-20TC-1156 Chemically Coupled Polypropylene Compound, 20% Talc Filled
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.5 PHR Sulfur
- Arlon 55276R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved