3M Dyneon™ Aflas® FA-150E PTFE Fluoroelastomer (discontinued **)

Category	Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Dyneon™ Aflas® FA-150E PTFE Fluoroelastomer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 57%F in polymer with 19% Medium Thermal Carbon Black (N990), 4% Triallyl Isocyanurate (TAIC), 1% Percadox™ 14, 1% Sodium Stearate. High speed extrusions. Improved flow for calendering and molding. Used in Aggressive Oil/Coolant/Base Resistant Applications.

Physical Properties	Metric	English	Comments
Density	1.55 g/cc	0.0560 lb/in³
Oxygen Transmission	150 cc-mm/m²-24hr-atm	381 cc-mil/100 in²-24hr-atm
Mooney Viscosity	60 @Temperature 100 °C	60 @Temperature 212 °F	ML1+10

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	70	70
Tensile Strength, Ultimate	13.0 MPa	1890 psi
Tensile Strength, Yield	2.70 MPa	392 psi	M100
Elongation at Break	370 %	370 %
Coefficient of Friction, Dynamic	0.70	0.70
Compression Set	48 % @Temperature 200 °C	48 % @Temperature 392 °F	70 hr; ASTM D395B

Thermal Properties	Metric	English	Comments
CTE, linear	240 µm/m-°C @Temperature 20.0 °C	133 µin/in-°F @Temperature 68.0 °F
Specific Heat Capacity	1.67 J/g-°C	0.399 BTU/lb-°F
Thermal Conductivity	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F
Glass Transition Temp, Tg	2.00 °C	35.6 °F	TR10

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+15 - 1.00e+16 ohm-cm	1.00e+15 - 1.00e+16 ohm-cm
Dielectric Constant	2.5 @Frequency 6.00e+7 Hz	2.5 @Frequency 6.00e+7 Hz
Dielectric Strength	23.0 kV/mm	584 kV/in