- A. Schulman ComAlloy Hiloy® 272 Polystyrene Alloy, Glass Reinforced, Flow Enhanced
A. Schulman ComAlloy Hiloy® 272 Polystyrene Alloy, Glass Reinforced, Flow Enhanced
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Glass Filled |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 272 Polystyrene Alloy, Glass Reinforced, Flow Enhanced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 72.0 MPa | 10400 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 6.40 GPa | 928 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 216 - 241 °C | 421 - 466 °F |
Users viewing this material also viewed the following:
- Michelman® Michem® Emulsion 39235 Nonionic high density polyethylene emulsion
- Lucas-Milhaupt Silvaloy® A50N Flux Coated Rod Brazing Alloy
- Sax Polymers SAXAMID 226F10 Nylon 6.6, 50% Glass Fiber
- A. Schulman PP 1452 Polypropylene Medium Impact Polypropylene
- A. Schulman PAPERMATCH® T-4338/50 Specialty Masterbatch
- Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 52%/G1177 Glass/Carbon Fiber
- ConocoPhillips Syncon® 68 Synthetic AW Hydraulic Fluid 68
- DuPont Teijin Films Mylar® EL Polyester Film, 48 Gauge
- 3M Scotch-Weld™ 3796 Hot Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved