- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Diamond Polymers ASA TW-18B1
Diamond Polymers ASA TW-18B1
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ASA TW-18B1.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Very High HeatInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A; ASTM D1238 |
| 1.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 | |
| 2.9 g/10 min @Load 10.0 kg, Temperature 220 °C |
2.9 g/10 min @Load 22.0 lb, Temperature 428 °F |
Procedure A; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 50.86 MPa | 7376 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.51 GPa | 364 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | 0.125 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 |
| 115 °C | 239 °F | 0.25 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 | |
| Vicat Softening Point | 133 °C | 271 °F | 0.125 inch, 1 Kg; ASTM D1525 |
Users viewing this material also viewed the following:
- Total Finaprene® 502 Styrene-Butadiene TPE Copolymer (discontinued **)
- LG Chemical Lupoy 1302EP-30 Polycarbonate Resin
- Multibase Multi-Flex® A 2599 TPE Thermoplastic Elastomer
- Stir SpA RI 57 PLA (PVC)
- Unipetrol PP MONSTEN® MA 612 Polypropylene Impact Copolymer
- Wellman Wellamid® XT1627-WBK2 High Impact, Weatherable Nylon 66
- DuPont Teijin Films Melinex® 473 Polyester Film, 200 Gauge
- Denka LCS Z6060 Thermoplastic Elastomer, Injection Molding Grade (general)
- Braskem GM7040G HDPE High Density Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved