Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 23.0 °C |
1.00e+14 ohm-cm @Temperature 73.4 °F |
ASTM D257 |
DuPont Performance Polymers Crastin® 6130 NC010 PBT
(Unverified Data**) Crastin® 6130 NC010 is an unreinforced, medium high viscosity polybutylene terephthalate resin for extrusion and injection molding.Information provided by DuPont Performance Polymers |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
|
Master Bond EP112LS Two part, heat curing epoxy for potting, encapsulation, coating, sealing and impregnation Master Bond EP112LS is a low viscosity two component epoxy resin system for potting, encapsulation, sealing, coating and impregnation. The mix ratio is an easy to use 100:80 by weight. EP112LS offer.. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CeramTec 665 Steatite, MgO•SiO2 Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. 665 L533C has low dielectric loss. It makes exc.. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 100 °C |
1.00e+14 ohm-cm @Temperature 212 °F |
IEC 672-1 |
CeramTec 665 Steatite, MgO•SiO2 Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. 665 L533C has low dielectric loss. It makes exc.. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 25.0 °C |
1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CeramTec 701 Cordierite Cordierites have low coefficients of thermal expansion and excellent resistance to thermal shock. They offer a range of thermal expansion, mechanical strength, and porosity criteria. They excel as c.. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec B 601 Alumina, 98.5% Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec DN 70 Dispersion Ceramic, Al2O3-ZrO2 DN 70 is a ZTA Alumina Toughened Zirconia. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 20.0 °C |
>= 1.00e+14 ohm-cm @Temperature 68.0 °F |
|
CeramTec Rubalit® A 1894 Alumina, 94% Rubalit® A 1894 (94%) was specifically developed in response to electrical and electronic engineering needs. In conjunction with CeramTec's complementary metallization systems, a vacuum-tight bond .. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 20.0 °C |
>= 1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec Rubalit® IS 95 Alumina Rubalit® IS 95 is a high-performance alumina ceramic. Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at eleva.. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec V 679 Alumina, 99.7% Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CoorsTek ADS-995 99.5% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CoorsTek ADS-996 99.6% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D1829 |
CoorsTek PlasmaPure-UC™ 99.9% Alumina |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CoorsTek Superstrate® 996 99.6% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 300 °C |
>= 1.00e+14 ohm-cm @Temperature 572 °F |
ASTM-D257 |
CoorsTek Superstrate® TPS 99.6% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
|
Anderman Ceramics EA95 Sintered Alumina, 95% Densely sintered alumina is characterized by: high strength and hardness, temperature stability, electrical insulation, and high wear resistance and corrosion resistance even at high temperatures. .. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
|
Anderman Ceramics EA96 Sintered Alumina, 96% High strength alumina (96%) available pink or white. Available in many shapes and sizes.Information provided by Anderman Ceramics. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 25.0 °C |
1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM D257 |
3M Scotchcast™ 265 Electrical Epoxy Powder Resin 3M Scotchcast Electrical Resin 265 is a new solution to an old problem. Historically, manufactures of coils, stators and armatures have used liquid-based varnishes or resins to coat and impregnate t.. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
|
Anderman Ceramics EA995 Sintered Alumina, 99.5% Densely sintered alumina is characterized by: high strength and hardness, temperature stability, electrical insulation, and high wear resistance and corrosion resistance even at high temperatures. .. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
|
Anderman Ceramics EAZ 20 Zirconia Toughened Alumina Zirconia materials offer high temperature capability as well as excellent performance in areas of high wear and corrosion. Available in many shapes and sizes. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 25.0 °C |
1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CeramTec 447 Cordierite, 2MgO•Al2O3•5SiO2 Cordierites have low coefficients of thermal expansion and excellent resistance to thermal shock. They offer a range of thermal expansion, mechanical strength, and porosity criteria. They excel as c.. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 20.0 °C |
>= 1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec Rubalit® A 1896 Alumina Rubalit® A 1896 (96%) is an aluminum oxide ceramic with an optimum price/performance ratio. Its outstanding properties are low density, low weight, high corrosion and wear resistance, excellent ele.. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 20.0 °C |
>= 1.00e+14 ohm-cm @Temperature 68.0 °F |
|
CeramTec Rubalit® A 1898 Alumina, 98% Rubalit® A 1898 (98%) was specifically developed in response to electrical and electronic engineering needs. In conjunction with CeramTec's complementary metallization systems, a vacuum-tight bond .. |