CeramTec B 601 Alumina, 98.5%
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | CeramTec North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CeramTec B 601 Alumina, 98.5%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.83 g/cc | 0.138 lb/in³ | DIN EN 623-2 |
| Water Absorption | 0.00 % | 0.00 % | Open Porosity; DIN EN 623-2 |
| Permeability | 0.00 | 0.00 | %, Gas |
| Weibull Modulus | 10 | 10 | DINV ENV 843-5 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 1600 | 1600 | HV1; DINV ENV 843-4 |
| Tensile Modulus | 320 GPa | 46400 ksi | Young's; DINV ENV 843-2 |
| Flexural Strength | 390 MPa | 56600 psi | DIN EN 843-1 |
| Compressive Strength | 2000 MPa | 290000 psi | DIN 51067T1 |
| Poissons Ratio | 0.22 | 0.22 | DINV ENV 843-2 |
| Fracture Toughness | 4.90 MPa-m½ | 4.46 ksi-in½ | K<sub>IC</sub> (SEVNB); DIN CEN/TS 14425-1 |
| Shear Modulus | 131 GPa | 19000 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.30 µm/m-°C @Temperature 20.0 - 400 °C |
4.06 µin/in-°F @Temperature 68.0 - 752 °F |
DIN EN 821-1 |
| 8.70 µm/m-°C @Temperature 20.0 - 1000 °C |
4.83 µin/in-°F @Temperature 68.0 - 1830 °F |
DIN EN 821-1 | |
| Specific Heat Capacity | 0.900 J/g-°C | 0.215 BTU/lb-°F | DINV ENV 821-3 |
| Thermal Conductivity | 24.0 W/m-K | 167 BTU-in/hr-ft²-°F | DIN EN 821-2 |
| Maximum Service Temperature, Air | 1300 °C | 2370 °F | |
| Maximum Service Temperature, Inert | 1300 °C | 2370 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 98.5 % | 98.5 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm @Temperature 400 °C |
1.00e+10 ohm-cm @Temperature 752 °F |
IEC 672-1 |
| 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 | |
| Dielectric Constant | 9.0 @Frequency 1.00e+6 Hz |
9.0 @Frequency 1.00e+6 Hz |
IEC 672-1 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 672-1 |
| Dielectric Loss Index | 0.0060 @Frequency 9.00e+9 Hz |
0.0060 @Frequency 9.00e+9 Hz |
IEC 672-1 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ra = Arithmetic Mean Roughness Value (µm) | <0.2 | |
| Thermal Shock Resistance R1 (K) | 101 | calculated; R1 = [s? (1-µ)] / (a·E) |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MS 26 A Linear Low Density Polyethylene
- Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA), 15% Glass Fiber (Conditioned)
- Saint-Gobain Chemlam® 2200 Multi-plied, Flexible, Non-porous Fluoropolymer Laminated Composite
- Formosa Plastics Formolene® L62009H Film (Hexene Grade) LLDPE
- Chosun Refractories HM-S Special Mortar for Sliding Gate Valve
- Chosun Refractories CFA-2 Ceramic Foam
- BASF Elastollan R 2005/1 20% Glass Filled TPUR
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 78A
- DuPont Performance Polymers Crastin® LW9330 NC010 PBT (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved