CoorsTek Superstrate® TPS 99.6% Alumina Thin Film
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | CoorsTek |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CoorsTek Superstrate® TPS 99.6% Alumina Thin Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: thin film substrates
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.95 g/cc | 0.143 lb/in³ | ASTM-C373 |
| Water Absorption | 0.00 % | 0.00 % | ASTM-C373 |
| Particle Size | <= 1.0 µm | <= 1.0 µm | Grain Size |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell 45 N | 87 | 87 | ASTM-E18 |
| Modulus of Elasticity | 372 GPa | 54000 ksi | ASTM-C848 |
| Flexural Strength | 682 MPa | 98900 psi | ASTM-F394 |
| Poissons Ratio | 0.20 | 0.20 | ASTM-C848 |
| Shear Modulus | 155 GPa | 22500 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 6.30 µm/m-°C @Temperature 25.0 - 300 °C |
3.50 µin/in-°F @Temperature 77.0 - 572 °F |
ASTM-C372 |
| 7.20 µm/m-°C @Temperature 25.0 - 600 °C |
4.00 µin/in-°F @Temperature 77.0 - 1110 °F |
ASTM-C372 | |
| 7.90 µm/m-°C @Temperature 25.0 - 800 °C |
4.39 µin/in-°F @Temperature 77.0 - 1470 °F |
ASTM-C372 | |
| 8.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.56 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM-C372 | |
| Thermal Conductivity | 27.0 W/m-K @Temperature 100 °C |
187 BTU-in/hr-ft²-°F @Temperature 212 °F |
ASTM-C408 |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 99.6 % | 99.6 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+10 ohm-cm @Temperature 700 °C |
>= 1.00e+10 ohm-cm @Temperature 1290 °F |
ASTM-D257 |
| >= 1.00e+12 ohm-cm @Temperature 500 °C |
>= 1.00e+12 ohm-cm @Temperature 932 °F |
ASTM-D257 | |
| >= 1.00e+14 ohm-cm @Temperature 300 °C |
>= 1.00e+14 ohm-cm @Temperature 572 °F |
ASTM-D257 | |
| >= 1.00e+15 ohm-cm @Temperature 25.0 °C |
>= 1.00e+15 ohm-cm @Temperature 77.0 °F |
ASTM-D257 | |
| >= 1.00e+15 ohm-cm @Temperature 100 °C |
>= 1.00e+15 ohm-cm @Temperature 212 °F |
ASTM-D257 | |
| Dielectric Constant | 9.9 @Frequency 1.00e+6 Hz |
9.9 @Frequency 1.00e+6 Hz |
ASTM-D150 |
| Dielectric Strength | 19.7 kV/mm @Thickness 1.02 mm |
500 kV/in @Thickness 0.0400 in |
ASTM-D149 |
| 25.2 kV/mm @Thickness 0.635 mm |
640 kV/in @Thickness 0.0250 in |
ASTM-D116 | |
| Dielectric Loss Index | 0.00010 @Frequency 1.00e+6 Hz |
0.00010 @Frequency 1.00e+6 Hz |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White | |
| Permeability | NIL | |
| Surface Finish - (µin.) | <1 | Polished; Profilometer, 0.004" Radius Stylus, 0.30" Cutoff, ANSI/ASME B46.1 |
| <10 | Lapped; Profilometer, 0.004" Radius Stylus, 0.30" Cutoff, ANSI/ASME B46.1 |
Users viewing this material also viewed the following:
- Renegade Materials Corporation RM-5001 Cyanate Ester Prepreg, 3K 8HS Fabric
- Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
- Ineos ABS TRIAX® 1220 S ABS/Nylon Blend, Dry as Molded
- SABIC Innovative Plastics LNP LUBRICOMP RFP36S PA 66
- Spartech Soft Touch HDPE Polyolefin Skin/Specialty Sheet
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- Cosmic Plastics D45 Mineral Filled Ortho Diallyl Phthalate Molding Compound
- Aaron Industries AAROPRENE® GFPC 5010 Glass Filled Polycarbonate
Copyright © lookpolymers.com All Rights Reserved