Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 120 min | 2.00 hour | Functional cure |
ITW Devcon 2 Ton® Epoxy Clear Epoxy, Clear, White Information provided by ITW Devcon |
|||
Cure Time | 120 - 240 min | 2.00 - 4.00 hour | Functional cure |
ITW Devcon Plastic Welderâ„¢ Methacrylate Adhesive SD, Off-White Information provided by ITW Devcon |
|||
Cure Time | 120 min | 2.00 hour | On-Part Life |
Loctite® 7380 Monomer Base Activator Surface PreparersLoctite offers a complete line of surface preparation products to ensure the maximum performance of Loctite® Adhesives and Sealants.Loctite® Accelerators are used to increase the .. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 32580B035 0.035" (0.889 mm) Uncured Silicone Rubber on PET Carrier Design/Construction: Interleave: PolyethyleneSide 1: Uncured Silicone RubberCarrier: PETThis data represents typical values for the production material. The data should not be used to write, or in p.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
Arlon 51044R020 0.020" Semi-Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 2.5 mil PolyethyleneSide 1: Semi-cured Silicone RubberSubstrate: Style 7628 FiberglassThis data represents typical values for the production material and should no.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 51571R018 0.018" (0.457 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Uncured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone RubberInterleave: Polyethylene Appearance: Black silicone gum on fiberglass clothThis da.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 51583R020 0.020" (0.508 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSide 2: Cured Silicone RubberThis data Represents typical values for the production material. The data should not be used to write, or in place of, m.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 51586R015H 0.016" (0.406 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 7628 Fiberglass Side 2: Uncured Silicone Rubber Interleave: Polyethylene This data represents typical values for the production mat.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
Arlon 55572GA028 0.028" Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: LDPESide 1: Cured Silicone RubberSubstrate: Style 162 FiberglassThis data represents typical values for the production material and should not be used as material .. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
Arlon 55578GA028 0.0280" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: LDPESide 2 Layer 2: Uncured Silicone RubberSide 2 Layer 1: Cured Silicone RubberSubstrate: Style 162 FiberglassSide 1: Cured Silicone RubberThis data represents ty.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
Arlon 55986C028 0.0295" Cured/Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave 1: N/ASide 1: Cured Silicone RubberSubstrate: Style 162 FiberglassSide 2: Uncured Silicone RubberInterleave 2: LDPEThis data represents typical values for the pro.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon CP-498W Bulk Compound This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Di.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon R32031R014 0.014" (0.356 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone Rubber Side 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place.. |
|||
Cure Time | 120 - 240 min | 2.00 - 4.00 hour | Tack Free Time, catalyzed with Moldmaster Red |
ACC QM 2128 QSI Quantum Silicones 28 Durometer Condensation Cure Moldmaking Material QM 2128 is a two-component, room temperature condensation cure silicone material. The cured rubber has excellent mechanical properties and good shelf-life stability. This material is an excellent ch.. |
|||
Cure Time | 120 min | 2.00 hour | Touch Dry |
3M Scotchkote™ FG 514 Urethane Ceramic Lining Scotchkote Urethane Ceramic Lining FG 514 has been specifically developed as a 100% solids polyceramic coating with a degree of flexibility for lining and resurfacing equipment operating in fluid fl.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 32580R060 0.060" (1.52 mm) Uncured Silicone Rubber on PET Carrier Design/Construction: Interleave: PolyethyleneSide 1: Uncured Silicone RubberCarrier: PETAppearance: Red silicone gum on polymer linerThis data represents typical values for the production material. .. |
|||
Cure Time | 120 - 180 min | 2.00 - 3.00 hour | Tack-Free, 50% RH |
3M 551 Polyurethane Adhesive Sealant 3M™ 500-Series Polyurethane Construction Sealant, Polyurethane Sealant and Polyurethane Adhesive Sealant products are one component, moisture curing products which form permanent elastic bonds. The.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 51149R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: Polyethylene Layer 2: Uncured Silicone RubberSubstrate: Style 7628 FiberglassLayer 1: Cured Silicone RubberThis data represents typical values for the production mat.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 51576R016A 0.016" (0.406 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: Polyethylene Side 1: Cured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone Rubber This data represents typical values for the production mat.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 51576R027 0.027" (0.686 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: Polyethylene Side 1: Cured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone Rubber This data represents typical values for the production mat.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
Arlon 51581R018 0.018" Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 3 mil PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Prime Coated 7628 FiberglassSide 2: Uncured Silicone RubberThis data represents typical values for the.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 51986XA015 0.016" (0.406 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 7628 Fiberglass Side 2: Uncured Silicone Rubber Interleave: Polyethylene Appearance: Gray silicone gum and rubber on fiberglass clo.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
|
Arlon 56946C026 Silicone Rubber/Fiberglass Laminate Side 1: cured silicone rubber; Substrate: 1564 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene |
|||
Cure Time | 120 - 240 min | 2.00 - 4.00 hour | Tack Free Time, catalyzed with Moldmaster Red |
ACC QM 2125 QSI Quantum Silicones 25 Durometer Condensation Cure Moldmaking Material QM 2125 is a two-component, room temperature condensation cure silicone material. The cured rubber has excellent mechanical properties and good shelf-life stability. This material is an excellent ch.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 44602M020 0.020" (0.508 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberAppearance Tan rubber on glass fiber fabricThis data represents typical values for the production material. The data should not be used to write, or .. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 31140R020 0.020" (0.508 mm) Uncured Fluorosilicone Rubber on Release Carrier Design/Construction: Interleave: PolyethyleneProduct: Uncured Fluorosilicone Rubber Carrier: Release coated HDPE Product Use: Flexible heater insulationAppearance: Red silicone gum on polymer releas.. |
|||
Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
Arlon 44570R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Layers Silicone Rubber Appearance: Red silicone gum on fiberglass clothThis data represents typical values for the production material. The data should not be use.. |