Arlon 51044R020 0.020" Semi-Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51044R020 0.020" Semi-Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Interleave: 2.5 mil PolyethyleneSide 1: Semi-cured Silicone RubberSubstrate: Style 7628 FiberglassThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 |
| 305 microns | 12.0 mil | Silicone; Arlon SQA-TMS-003 | |
| 508 microns | 20.0 mil | Overall Thickness; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 62 | 62 | Silicone Property; Arlon SQA-TMS-014 |
| Tensile Strength | 7.481 MPa | 1085 psi | Silicone Property; Arlon SQA-TMS-008 |
| Elongation at Break | 429 % | 429 % | Silicone Property; Arlon SQA-TMS-008 |
| Peel Strength | 2.44 kN/m | 13.9 pli | Bond Strength; Arlon SQA-TMS-011 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 204 °C | 400 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 28.7 kV/mm | 730 kV/in | Arlon SQA-TMS-020 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 3.00 Month @Temperature 21.1 °C |
3.00 Month @Temperature 70.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 20.6 | Arlon SQA-TMS-025 |
Users viewing this material also viewed the following:
- MV Labs HG400 HgCl2 Mercury(II) chloride
- Dow INSPIRE™ DT701-14 TPO (discontinued **)
- ExxonMobil LD 051.LT Shrink Film Resin (discontinued **)
- Materion BrushCAST® 20C High Strength Casting Alloy (As Cast & Aged)
- Lucas-Milhaupt HANDY HI-TEMP 548® Carbide Brazing Alloy
- Chase Plastics CP Pryme® PC310R Polycarbonate, 10% Glass Fiber Reinforced, Recycled Content
- Wellman Wellamid® XT1482-N Impact Modified Nylon 66, Lubricated & Heat Stabilized
- Covestro Desmopan® DP 8798A Polyurethane
- Covestro Makrolon® 9415 Polycarbonate, 10% Glass Filled
- AK Steel 410S Ferritic Stainless steel