- Polymer Property : CTE, linear = 20.0 µin/in-°F
Polymer Property : CTE, linear = 20.0 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 149 °C |
20.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
| Quadrant EPP Nylatron® GF30 Nylon Type 66, 30% Glass-Reinforced Black Color (ASTM Product Data Sheet) |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
| North Wood Plastics Polypropylene with 60% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
| North Wood Plastics Polypropylene with 60% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Ravago Manufacturing Americas Hylon® N2017THL Nylon 6 (DAM) Information provided by Ravago. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 149 °C |
20.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
| Quadrant EPP Duratron® PAI T4501 Polyamide-imide, compression molded bearing grade (ASTM Product Data Sheet) |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
| North Wood Plastics HDPE with 60% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
| North Wood Plastics PS with 40% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| PolyOne Edgetek® AS-20GF/000 HI UV NAT Acrylonitrile Butadiene Styrene (ABS), Glass Filled
(discontinued **)& Description/Features:Glass Fiber ReinforcedHigh ImpactUV StabilizedNaturalUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| CTE, linear | 36.0 - 99.0 µm/m-°C | 20.0 - 55.0 µin/in-°F | Average value: 64.3 µm/m-°C Grade Count:3 |
| Overview of materials for High Density Polyethylene (HDPE), Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Wood Filled". Each property range of values reported is minimum and ma.. |
|||
| CTE, linear | 36.0 - 216 µm/m-°C | 20.0 - 120 µin/in-°F | Average value: 139 µm/m-°C Grade Count:76 |
| Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
| Premix Premi-Glas® 8102-20 Glass Reinforced Polyester BMC
(discontinued **) Description: Premi-Glas® 8102-20 is a glass reinforced thermoset polyester Bulk Molding Compound designed for injection molding of automotive forward lighting reflectors. Key features and benefits:.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
| Premix Premi-Glas® 8105 Glass Reinforced Polyester BMC
(discontinued **) Description: Premi-Glas® 8105 is a glass reinforced thermoset polyester Bulk Molding Compound designed for injection molding of automotive forward lighting reflectors. Key features and benefits: Ex.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
| Premix Premi-Glas® 8201-24 Glass Reinforced Polyester SMC
(discontinued **) Description: Premi-Glas® 8201-24 is a low profile glass reinforced polyester Sheet Molding Compound designed for body panel applications.Key features and benefits: Compatible with in-mold coatings,.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
| Indium Corp. Indalloy® 209 Sn-Ag-Sb Solder Alloy Low temperature die attach alloy. Has very high tensile strength. Old Motorola die attach solder; very brittle.Information provided by the manufacturer, Indium Corporation. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 35.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 95.0 °F |
ASTM D696 |
| MRC Polymers NAXELLâ„¢ PC23M-10G General Purpose Polycarbonate, 10% Glass Fiber Filled, Low Viscosity Can be impact modifiedInternal and external lubricant can be addedBlack onlyInformation provided by MRC Polymers Inc. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature -30.0 - 100 °C |
20.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| LyondellBasell Hifaxâ„¢ CB272 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CB272 high melt flow, 900 MPa flexural modulus, low CLTE, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of rigidity and dime.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 30.0 - 150 °C |
20.0 µin/in-°F @Temperature 86.0 - 302 °F |
|
| Sumitomo Bakelite Durez® 31735 Phenolic, Compression Grade Durez 31735 is a special purpose phenolic molding compound developed for automotive and industrial pulleys. This material is designed to optimize pulley performance relating to belt life, dimension.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 30.0 - 150 °C |
20.0 µin/in-°F @Temperature 86.0 - 302 °F |
|
| Sumitomo Bakelite Durez® 31735 Phenolic, Injection Grade Durez 31735 is a special purpose phenolic molding compound developed for automotive and industrial pulleys. This material is designed to optimize pulley performance relating to belt life, dimension.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 120 °C |
20.0 µin/in-°F @Temperature -40.0 - 248 °F |
ASTM E831 |
| Azdel Plus C321-B01 32% Chopped Fiber Mat / PP Resin Matrix AZDEL® C321-B01 is a glass mat thermoplastic laminate based upon a random oriented chopped fiber mat contained within a polypropylene resin matrix. This composite material features high flow prope.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
| Armstrong C-1/H20 Epoxy Adhesive A versatile, low viscosity, unfilled resin used for electrical potting and laminating applications. It is an excellent insulator, and provides outstanding chemical resistance to most compoundsInfor.. |
|||
| CTE, linear | 36.0 - 45.0 µm/m-°C | 20.0 - 25.0 µin/in-°F | ASTM D696 |
| Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
| CTE, linear | 36.0 - 50.0 µm/m-°C | 20.0 - 27.8 µin/in-°F | Average value: 43.2 µm/m-°C Grade Count:5 |
| Overview of materials for Polyphenylene Ether, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 20% Glass Filled". Specific grades with glass content between 15% and 24% are inclu.. |
|||
| CTE, linear | 36.0 µm/m-°C | 20.0 µin/in-°F | DIN 52328 |
| Isoflon PAI Polyamideimide Materials with strong mechanical and electrical performances under high temperatures.Information provided by Isoflon. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
| Premix Premi-Glas® 1282-32 VE Glass Reinforced Vinyl Ester SMC
(discontinued **) Description: Premi-Glas® 1282-32 VE SMC is an enhanced high strength glass reinforced vinyl ester molding compound formulated for under-the-hood automotive applications.
Key features and benefi.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
| Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC
(discontinued **) Description: Premi-Glas® 1281-32 VE SMC is a high strength glass reinforced vinyl ester sheet molding compound formulated for under-the-hood automotive applications. Key features and benefits: Desi.. |
|||
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction |
| Premix Premi-Glas® 7203-28 28% Glass Reinforced Polyester SMC
(discontinued **) Description: Premi-Glas® 7203-28 is a low profile, 28% glass reinforced polyester Sheet Molding Compound designed for automotive structural vehicle body panel applications that require high flexura.. |
|||