Isoflon PAI Polyamideimide
| Category | Polymer , Thermoplastic , Polyamide-imide (PAI) , Polyamide-Imide, Extruded |
| Manufacturer | Isoflon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Isoflon PAI Polyamideimide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Materials with strong mechanical and electrical performances under high temperatures.Information provided by Isoflon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | DIN 53479 |
| Water Absorption | 0.33 % | 0.33 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 86 | 86 | ASTM D785 |
| Tensile Strength | 192 MPa | 27800 psi | DIN 53455 |
| Elongation at Break | 15 % | 15 % | DIN 53455 |
| Tensile Modulus | 4.90 GPa | 711 ksi | DIN 53457 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 36.0 µm/m-°C | 20.0 µin/in-°F | DIN 52328 |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous; DIN 52612 |
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | |
| Flammability, UL94 | V-0 @Thickness 1.17 mm |
V-0 @Thickness 0.0461 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Dielectric Constant | 4.2 @Frequency 1000 Hz |
4.2 @Frequency 1000 Hz |
DIN 53483 |
| Dielectric Strength | 23.0 - 25.0 kV/mm | 584 - 635 kV/in | DIN 53481 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Khaki |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1414H PC Copolymer (Asia Pacific)
- Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure
- SABIC Innovative Plastics LNP LUBRICOMP GL003XXP PSU (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal
- Taiwan Sheen Soon Sheenthane® AS-120 TPU for PU Adhesive
- Teknor Apex APEX® 07-U0296B-80 Polyvinyl Chloride, Flexible
- PlastxWorld Veroplas PA5300 Nylon 6
- Clariant Renol PA213G13 Nylon 6, 13% Glass Fiber, Heat Stabilized, Lubricated
- Asahi Glass Lumiflon LF-200 Solvent Soluble Fluoropolymer w/ Melamine hardening agent
- Overview of materials for Nylon 46, Lubricated + Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved