Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
North Wood Plastics Polypropylene with 60% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
North Wood Plastics Polypropylene with 60% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Ravago Manufacturing Americas Hylon® N2017THL Nylon 6 (DAM) Information provided by Ravago. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 149 °C |
20.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
Quadrant EPP Duratron® PAI T4501 Polyamide-imide, compression molded bearing grade (ASTM Product Data Sheet) |
|||
CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 149 °C |
20.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
Quadrant EPP Duratron® PAI T4540 Polyamide-imide, compression molded (ASTM Product Data Sheet) |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
North Wood Plastics HDPE with 60% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
North Wood Plastics PS with 40% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
PolyOne Edgetek® AS-20GF/000 HI UV NAT Acrylonitrile Butadiene Styrene (ABS), Glass Filled
(discontinued **)& Description/Features:Glass Fiber ReinforcedHigh ImpactUV StabilizedNaturalUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
CTE, linear | 36.0 - 99.0 µm/m-°C | 20.0 - 55.0 µin/in-°F | Average value: 64.3 µm/m-°C Grade Count:3 |
Overview of materials for High Density Polyethylene (HDPE), Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Wood Filled". Each property range of values reported is minimum and ma.. |
|||
CTE, linear | 36.0 - 216 µm/m-°C | 20.0 - 120 µin/in-°F | Average value: 139 µm/m-°C Grade Count:76 |
Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
Premix Premi-Glas® 8102-20 Glass Reinforced Polyester BMC
(discontinued **) Description: Premi-Glas® 8102-20 is a glass reinforced thermoset polyester Bulk Molding Compound designed for injection molding of automotive forward lighting reflectors. Key features and benefits:.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
Premix Premi-Glas® 8105 Glass Reinforced Polyester BMC
(discontinued **) Description: Premi-Glas® 8105 is a glass reinforced thermoset polyester Bulk Molding Compound designed for injection molding of automotive forward lighting reflectors. Key features and benefits: Ex.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
Premix Premi-Glas® 8201-24 Glass Reinforced Polyester SMC
(discontinued **) Description: Premi-Glas® 8201-24 is a low profile glass reinforced polyester Sheet Molding Compound designed for body panel applications.Key features and benefits: Compatible with in-mold coatings,.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
Indium Corp. Indalloy® 209 Sn-Ag-Sb Solder Alloy Low temperature die attach alloy. Has very high tensile strength. Old Motorola die attach solder; very brittle.Information provided by the manufacturer, Indium Corporation. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 35.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 95.0 °F |
ASTM D696 |
MRC Polymers NAXELLâ„¢ PC23M-10G General Purpose Polycarbonate, 10% Glass Fiber Filled, Low Viscosity Can be impact modifiedInternal and external lubricant can be addedBlack onlyInformation provided by MRC Polymers Inc. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 30.0 - 150 °C |
20.0 µin/in-°F @Temperature 86.0 - 302 °F |
|
Sumitomo Bakelite Durez® 31735 Phenolic, Compression Grade Durez 31735 is a special purpose phenolic molding compound developed for automotive and industrial pulleys. This material is designed to optimize pulley performance relating to belt life, dimension.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 30.0 - 150 °C |
20.0 µin/in-°F @Temperature 86.0 - 302 °F |
|
Sumitomo Bakelite Durez® 31735 Phenolic, Injection Grade Durez 31735 is a special purpose phenolic molding compound developed for automotive and industrial pulleys. This material is designed to optimize pulley performance relating to belt life, dimension.. |
|||
CTE, linear | 36.0 µm/m-°C | 20.0 µin/in-°F | Below Tg |
Epoxy Technology EPO-TEK® B9021 Epoxy Paste Material Description: A single component, B-stageable epoxy paste for semiconductor, microelectronics, and optical assemblies. It can be used in hybrid assemblies for lid-sealing and substrate atta.. |
|||
CTE, linear | 36.0 µm/m-°C | 20.0 µin/in-°F | |
CMT Materials HYTAC® FLXT High Temperature, PTFE Impregnated Copolymer Syntactic HYTAC-FLXT is a unique material, combining the toughness and higher friction of FLX with improved release characteristic through PTFE impregnation. The result is a new, tough syntactic with just th.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 120 °C |
20.0 µin/in-°F @Temperature -40.0 - 248 °F |
ASTM E831 |
Azdel AZMET® CM32350 35% continuous random fiber mat / PET resin matrix AZDEL® CM20350 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a Polyethylene Terephthalate (PET) resin matrix. This composite material fea.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
|
Armstrong C-1/H20 Epoxy Adhesive A versatile, low viscosity, unfilled resin used for electrical potting and laminating applications. It is an excellent insulator, and provides outstanding chemical resistance to most compoundsInfor.. |
|||
CTE, linear | 36.0 - 45.0 µm/m-°C | 20.0 - 25.0 µin/in-°F | ASTM D696 |
Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
CTE, linear | 36.0 - 50.0 µm/m-°C | 20.0 - 27.8 µin/in-°F | Average value: 43.2 µm/m-°C Grade Count:5 |
Overview of materials for Polyphenylene Ether, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 20% Glass Filled". Specific grades with glass content between 15% and 24% are inclu.. |
|||
CTE, linear | 36.0 - 63.0 µm/m-°C | 20.0 - 35.0 µin/in-°F | Average value: 49.7 µm/m-°C Grade Count:6 |
Overview of materials for Polypropylene, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Wood Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
Z-direction; ASTM D696 |
Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC
(discontinued **) Description: Premi-Glas® 1281-32 VE SMC is a high strength glass reinforced vinyl ester sheet molding compound formulated for under-the-hood automotive applications. Key features and benefits: Desi.. |
|||
CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
PolyOne Edgetek® PS-20GF/000 FR Polybutylene Terephthalate (PBT), Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedIgnition ResistantUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation. |