SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing.

Physical Properties	Metric	English	Comments
Density	1.28 g/cc	0.0462 lb/inÂ³	ASTM D792
	1.28 g/cc	0.0462 lb/inÂ³	ISO 1183
Moisture Absorption	0.100 %	0.100 %	50% RH, 24 hrs; ASTM D570
	0.170 %	0.170 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
	42.0 MPa	6090 psi	ISO 527
Tensile Strength, Yield	51.0 MPa	7400 psi	ASTM D638
	53.0 MPa	7690 psi	ISO 527
Elongation at Break	22.6 %	22.6 %	ISO 527
	39.9 %	39.9 %	ASTM D638
Elongation at Yield	5.2 %	5.2 %	ASTM D638
	5.3 %	5.3 %	ISO 527
Tensile Modulus	2.33 GPa	338 ksi	1 mm/min; ISO 527
	2.42 GPa	351 ksi	50 mm/min; ASTM D638
Flexural Strength	82.0 MPa	11900 psi	ASTM D790
	83.0 MPa	12000 psi	ISO 178
Flexural Modulus	2.02 GPa	293 ksi	ISO 178
	2.10 GPa	305 ksi	ASTM D790
Izod Impact, Notched	1.33 J/cm	2.49 ft-lb/in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D4812
Izod Impact, Notched (ISO)	13.0 kJ/mÂ²	6.19 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	NB	NB	80104; ISO 180/1U
Dart Drop, Total Energy	30.0 J	22.1 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	72.0 J	53.1 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.18	0.18	ASTM D3702 Modified
Coefficient of Friction, Static	0.070	0.070	ASTM D3702 Modified
K (wear) Factor	121 x 10^-8 mmÂ³/N-M	60.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	121 Â°C	250 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	121 Â°C @Thickness 3.20 mm	250 Â°F @Thickness 0.126 in	unannealed; ASTM D648