Styron CALIBREâ„¢ IM 401 11 Polycarbonate, Impact Modified

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer Styron
Trade Name CALIBRE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ IM 401 11 Polycarbonate, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CALIBRE® IM401 series resins are impact modified, UL listed polycarbonate resins which contain mold release. CALIBRE IM401 polycarbonate resins exhibit an excellent balance of impact strength and heat resistance.CALIBRE IM401 polycarbonate resins are typically used in applications requiring enhanced impact strength, such as automotive instrument panel components and retainers.Available Melt Flow Rates: 11, 18.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM Data
Melt Density 1.02 g/cc
0.0368 lb/in³
Melt density
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Melt Flow 11 g/10 min

@Load 1.20 kg,
Temperature 300 °C
11 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM Data
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.8 MPa
8090 psi
ASTM Data
Elongation at Break 130 %
130 %
ASTM Data
Elongation at Yield 6.0 %
6.0 %
ISO Data
Tensile Modulus 2.20 GPa
319 ksi
ISO Data.
Izod Impact, Notched 6.94 J/cm
13.0 ft-lb/in
ASTM Data
5.34 J/cm

@Temperature -50.0 °C
10.0 ft-lb/in

@Temperature -58.0 °F
ASTM Data
Charpy Impact Unnotched NB
NB
ISO Data
NB
NB
ISO Data, Low Temp
Charpy Impact, Notched 4.00 J/cm²
19.0 ft-lb/in²
ISO Data, Low Temp
7.00 J/cm²
33.3 ft-lb/in²
ISO Data
Impact Test 56.5 J

@Temperature 23.0 °C
41.7 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
Specific Heat Capacity 1.76 J/g-°C
0.421 BTU/lb-°F
Thermal Conductivity 0.191 W/m-K
1.33 BTU-in/hr-ft²-°F
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Unannealed; 136°C (277°F) annealed; ASTM Data
Vicat Softening Point 146 °C
295 °F