| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 3.18 mm |
403 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne Nymax™ GF 600 A 33 Natural Polyamide 6 (Nylon 6) The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 6.35 mm |
403 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne Stat-Tech™ PI-05CF/000R Black Polyether Imide (PEI) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| Plenco 50015 PET, Pellet, Injection Molded, Black
(discontinued **) PLENCO 50015 is an engineering grade glass reinforced polyethylene terephthalate resin designed for increased flexibility and good physical strength. It is UL recognized and available in white, natu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Unannealed; ASTM D648 |
| LNP Thermocomp® EC-1006 EM Polyetherimide, Carbon Fiber Reinforcement
(discontinued **) Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are st.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 73G30T BK261 Nylon 6
(Unverified Data**) Zytel® 73G30T BK261 is a 30% glass fiber reinforced, toughened, black polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1/-2 |
| Lanxess Pocan® BF 4130 XF 700051 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding, flame retardant, improved flowability |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1,-2 |
| Gromax BFG20-FN00N1 Nylon 6 20% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP EX07305 PEI (Asia Pacific) Polyetherimide reinforced with Glass fiber and PTFE for use in Burn-in Test Sockets (BiTS) Application |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem 2200N PEI 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® ENH4565 PBT (Europe-Africa-Middle East) 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Stat-kon EE005 PEI (Asia Pacific) LNP STAT-KON* EE005 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON PFD06 PA 6 LNP* STAT-KON* PFD06 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp EF008E PEI (Asia Pacific) LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Asia Pac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PF006 PA 6 LNP THERMOCOMP* PF006 is a compound based on Nylon 6 resin containing 30% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp WC003 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WC003 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABI.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 LNP THERMOCOMP* PF006S is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1, 2 |
| Polyplastics Duranex® 3105H Polybutylene Terephthalate (PBT), Standard, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1, 2 |
| Polyplastics Duranex® 3226 Polybutylene Terephthalate (PBT), Standard, FR, UL approved regrind 50%, 20% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75 |
| Polyram RamSter PF305G6 PBT, 30% Glass Fiber 30% Glass fiber reinforced, PBT for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1, 2 |
| Polyplastics Duranex® 3105A Polybutylene Terephthalate (PBT), Epoxy adhesion improved, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GF33 33% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM Test |
| BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties in.. |
|||