SABIC Innovative Plastics LNP LUBRICOMP EX07305 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP EX07305 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyetherimide reinforced with Glass fiber and PTFE for use in Burn-in Test Sockets (BiTS) Application
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.506 g/cc | 0.05441 lb/in³ | ASTM D792 |
| 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0052 cm/cm | 0.0052 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 156 MPa | 22600 psi | 5 mm/min; ISO 527 |
| 157 MPa | 22800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.54 GPa | 1240 ksi | 1 mm/min; ISO 527 |
| 8.62 GPa | 1250 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 201 MPa | 29200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 202 MPa | 29300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.42 GPa | 931 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.21 GPa | 1050 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.670 J/cm | 1.26 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.29 J/cm | 6.16 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
7.83 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 50.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.60e+16 ohm-cm | 7.60e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 2.00e+13 ohm | 2.00e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 100000 Hz |
3.3 @Frequency 100000 Hz |
ASTM D150 |
| Dielectric Strength | 31.4 kV/mm @Thickness 1.60 mm |
798 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0031 @Frequency 100000 Hz |
0.0031 @Frequency 100000 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers XP44-11 PVC
- LG Chemical LUPOL HM-5204B High Modulus Polypropylene, 20% Polymer Alloy, High Strength, High Flow, High Modulus
- Sumitomo Bakelite North America 775 CAF Mineral Filled Diallyl Phthalate
- A. Schulman POLYBATCH™ FSU-105-E Concentrate Based In LDPE
- DuPont™ Elvax® 3190A Ethylene Vinyl Acetate
- Diamond Polymers NPP30-3500F Homopolymer Polypropylene
- ACC QM 270 QSI Quantum Silicones 70 Durometer Addition Cure Moldmaking Material
- Ineos Nova 201 Crystal Polystyrene High Heat Extrusion Grade (discontinued **)
- Hexcel® HexWeb® CR III 3/16-5052-.0015 Corrosion Resistant Specification Grade Aluminum Honeycomb
Copyright © lookpolymers.com All Rights Reserved