PolyOne Stat-Tech™ PI-05CF/000R Black Polyether Imide (PEI)

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	PolyOne Corporation
Trade Name	Stat-Tech™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Stat-Tech™ PI-05CF/000R Black Polyether Imide (PEI).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 g/cc	1.30 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	130 MPa	18900 psi	ASTM D638
Elongation at Break	4.2 %	4.2 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	6.06 GPa	879 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	212 MPa	30700 psi	ASTM D790
Flexural Modulus	5.96 GPa	864 ksi	ASTM D790
Izod Impact, Notched	0.530 J/cm @Thickness 6.35 mm, Temperature 23.0 °C	0.993 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	212 °C @Thickness 6.35 mm	414 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	206 °C @Thickness 6.35 mm	403 °F @Thickness 0.250 in	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 - 1.00e+12 ohm-cm	1.00e+10 - 1.00e+12 ohm-cm	ASTM D257
Surface Resistance	1.00e+10 - 1.00e+12 ohm	1.00e+10 - 1.00e+12 ohm	ASTM D257

Processing Properties	Metric	English	Comments
Melt Temperature	360 - 399 °C	680 - 750 °F

Descriptive Properties	Value	Comments
Features	Antistatic
Filler / Reinforcement	Carbon Fiber Reinforcement, 5.0% Filler by Weight
Forms	Pellets
Generic Material	PEI
Generic Name	Polyether Imide (PEI)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Aerospace Applications
	Automotive Electronics
	Business Equipment
	Computer Components
	Connectors
	Electrical Housing
	Electrical/Electronic Applications
	Housings