SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* PF006S is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.860 % | 0.860 % | 50% RH, 24 hrs; ASTM D570 |
| 1.53 % | 1.53 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0017 - 0.0050 cm/cm @Time 86400 sec |
0.0017 - 0.0050 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 128 MPa | 18600 psi | ISO 527 |
| 129 MPa | 18700 psi | ASTM D638 | |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| 2.9 % | 2.9 % | ISO 527 | |
| Tensile Modulus | 8.58 GPa | 1240 ksi | 1 mm/min; ISO 527 |
| 8.75 GPa | 1270 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 201 MPa | 29200 psi | ASTM D790 |
| 204 MPa | 29600 psi | ISO 178 | |
| Flexural Modulus | 6.96 GPa | 1010 ksi | ASTM D790 |
| 7.97 GPa | 1160 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 67.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 67.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C @Thickness 3.20 mm |
426 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 740S (RL) Synthetic Oil
- Polimeri Europa Edistir ICE R 830D Polystyrene
- Permabond UV670 UV-curable Adhesive
- Covestro Apec® DP9-9373 High-Heat Polycarbonate, General Purpose, UV-Stabilized (discontinued **)
- LyondellBasell Alathon® M5040 High Density Polyethylene
- Huntsman Araldite GY 6005 Bisphenol A Epoxy Liquid Resin
- SABIC Innovative Plastics ULTEM 8015 PEI (Asia Pacific)
- Loctite® 3873 1 component acrylic High Conductivity Flexible Adhesive
- DuPont Surlyn® PC2000 (discontinued **)
Copyright © lookpolymers.com All Rights Reserved