Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 324 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Plastcom SLOVALEN PH 49 GF 30 TS PP, 30% glass fibre, mod. of mech. Properties
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass fibre, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP...
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer
XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer (Asia Pacific)
XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® XHT4143T PC Copolymer (Asia Pacific)
XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Unannealed; ASTM D648
Solvay Specialty Polymers KetaSpire® KT-820P Polyetheretherketone (PEEK)  (Unverified Data**)
KetaSpire KT-820P is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color coarse powder form. KetaSpire PEEK is produced to the highest industry standards and is ..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Annealed; ASTM D648
Solvay Specialty Polymers KetaSpire® KT-850 Polyetheretherketone (PEEK)  (Unverified Data**)
KetaSpire KT-850 is the intermediate-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color pellet form. KetaSpire PEEK is produced to the highest industry standards and ..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Unannealed; ASTM D648
Solvay Specialty Polymers KetaSpire® KT-850P Polyetheretherketone (PEEK)  (Unverified Data**)
KetaSpire KT-850P is the intermediate-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color coarse powder form. KetaSpire PEEK is produced to the highest industry standa..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
ASTM D648
LATI LATAN 13 G/303 30% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM)  (discontinued **)
Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
ASTM D648
LATI LATAN 13 K/30 30% Carbon Fiber Reinforced Polyoxymethylene Copolymer (POM)  (Unverified Data**)
Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C

@Thickness 3.17 mm
324 °F

@Thickness 0.125 in
ASTM D648
Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant  (discontinued **)
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer (Asia Pacific)
XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA6.12
LNP LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C

@Thickness 3.20 mm
324 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copolymer
LNP* Lubricomp* KFL22 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP f..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Unannealed; ASTM D648
Solvay Specialty Polymers KetaSpire® KT-820P Polyetheretherketone (PEEK)
KetaSpire® KT-820P is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color coarse powder form. KetaSpire® PEEK is produced to the highest industry standards..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Annealed; ASTM D648
Solvay Specialty Polymers KetaSpire® KT-850 Polyetheretherketone (PEEK)
KetaSpire® KT-850 is the intermediate-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color pellet form. KetaSpire® PEEK is produced to the highest industry standa..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Unannealed; ASTM D648
Solvay Specialty Polymers KetaSpire® KT-850P Polyetheretherketone (PEEK)
KetaSpire® KT-850P is the intermediate-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color coarse powder form. KetaSpire® PEEK is produced to the highest industr..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C

@Thickness 3.20 mm
324 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP KF005 Acetal Copolymer
LNP THERMOCOMP* KF005 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber. Added features of this material include: Chemically Coupled.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp OX92080 PPS - LINEAR
LNP* Thermocomp* OX92080 is a compound based on Linear PPS containing Proprietary Fillers.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6
LNP THERMOCOMP* PH0600A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp SF006S PA 12
LNP* Thermocomp* SF006S is a compound based on Nylon 12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas re..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
ASTM D648
Zhejiang Double Fish YS-G050 50% Long Fiber Glass Reinforced Polypropylene
Features high strength, good surface quality, and easy processing. Typical applications include automobile (bumper back beam, arm rest core, instrument panel, mudflap), machinery, electronics, comm..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Covestro Apec® HT KU 1-9350 High-Heat Polycarbonate
Transparent and opaque shades possible.Applications: Medical sector: superheated steam sterilization.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Ba..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Covestro Apec® HT KU 1-9351 High-Heat Polycarbonate
Transparent and opaque shades possible.Applications: Lighting, automotive and household goods, light covers, indicator and brake light lenses.Information provided by Bayer.As of 1 September 2015, Ba..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Conditioned)
Designation ISO 1874-PA12,M,16-120,CF30Rigid grade with carbon fiber filler (30%) for injection molding. Available color: black.Very high rigidity. High strength-to-weight ratio. Very low shrinkage:..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
ISO 75
Azoty Tarnow™ TARNOFORM 300 GF5 POM
26% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A...
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
ISO 75
Azoty Tarnow™ TARNOFORM 300 GF6 BK POM
30% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A...
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Asahi Kasei Thermylene® P7-20FG-0876 Chemically Coupled Polypropylene Compound, 20% Glass Filled
Applications: Automotive: Sun Roof Rails, Fan Shrouds, Air Cleaners, Battery Boxes, Air Induction Components, Battery Trays, Blower Wheels, Light Housings, Shifter Bases, Interior Consoles, Arm Rest..
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
ASTM D648
E-Polymers Tekaloy® T80G20 , 20% Glass Fiber Reinforced PBT/ABS Alloy
20% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd.
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
ISO 75-2
BASF Ultradur B 4300 G2 High Speed Unc. 10% Glass Filled PBT
Ultradur B 4300 G2 High Speed Unc. is a high flow, fast cycling with low warpage, 10% glass filled, pigmented black, injection molding PBT for industrial parts, rigid tough and dimensional stable ap..