Azoty Tarnow™ TARNOFORM 300 GF5 POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced
Manufacturer	Azoty Tarnow™ (Zaklady Azotowe)
Trade Name	TARNOFORM
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Azoty Tarnow™ TARNOFORM 300 GF5 POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

26% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.

Physical Properties	Metric	English	Comments
Density	1.59 g/cc	0.0574 lb/in³	ISO 1183
Water Absorption	0.51 %	0.51 %	ISO 62
Linear Mold Shrinkage	0.0102 cm/cm @Thickness 4.00 mm	0.0102 in/in @Thickness 0.157 in
Linear Mold Shrinkage, Transverse	0.0205 cm/cm	0.0205 in/in	60x60x4; ISO 294-4
Melt Flow	5.0 g/10 min @Load 2.16 kg, Temperature 190 °C	5.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	196 MPa	28400 psi	358 N; ISO 2039-1
Tensile Strength at Break	115 MPa	16700 psi	ISO 527
Elongation at Break	3.5 %	3.5 %	ISO 527
Tensile Modulus	8.90 GPa	1290 ksi	ISO 527
Flexural Strength	173 MPa	25100 psi	ISO 178
Izod Impact, Notched (ISO)	7.10 kJ/m²	3.38 ft-lb/in²	1A; ISO 180
Charpy Impact, Notched	0.590 J/cm²	2.81 ft-lb/in²	1eA; ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	167 °C	333 °F	10°C/min.; ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	162 °C	324 °F	ISO 75
Vicat Softening Point	161 °C	322 °F	50 N; ISO 306
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	IEC 60093
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 60093
Dielectric Constant	4.2 @Frequency 100 Hz	4.2 @Frequency 100 Hz	IEC 60250
	4.2 @Frequency 1e+6 Hz	4.2 @Frequency 1e+6 Hz	IEC 60250
Dielectric Strength	30.0 kV/mm	762 kV/in	IEC 60243
Dissipation Factor	0.0095 @Frequency 1e+6 Hz	0.0095 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 112

Processing Properties	Metric	English	Comments
Processing Temperature	180 - 230 °C	356 - 446 °F	Barrel temperature
Mold Temperature	60.0 - 120 °C	140 - 248 °F