Covestro Apec® HT KU 1-9350 High-Heat Polycarbonate

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, High Heat
Manufacturer	Covestro
Trade Name	Apec®
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Covestro Apec® HT KU 1-9350 High-Heat Polycarbonate.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Transparent and opaque shades possible.Applications: Medical sector: superheated steam sterilization.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/in³
Water Absorption	0.40 %	0.40 %	Saturation in water
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Equilibrium at 50% RH
Water Absorption at Saturation	0.40 %	0.40 %
Melt Flow	8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 330 °C	8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 626 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	65.0 MPa	9430 psi
Elongation at Break	>= 50 %	>= 50 %	Nominal
Elongation at Yield	7.0 %	7.0 %
Tensile Modulus	2.30 GPa	334 ksi
Charpy Impact Unnotched	NB	NB
	0.800 J/cm² <br>@Temperature -30.0 °C	3.81 ft-lb/in² <br>@Temperature -22.0 °F
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	70.0 µm/m-°C <br>@Temperature 20.0 °C	38.9 µin/in-°F <br>@Temperature 68.0 °F
CTE, linear, Transverse to Flow	70.0 µm/m-°C <br>@Temperature 20.0 °C	38.9 µin/in-°F <br>@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	174 °C	345 °F
Deflection Temperature at 1.8 MPa (264 psi)	162 °C	324 °F
Vicat Softening Point	183 °C	361 °F
Flammability, UL94	HB <br>@Thickness 1.60 mm	HB <br>@Thickness 0.0630 in
	HB <br>@Thickness 3.00 mm	HB <br>@Thickness 0.118 in
Oxygen Index	24 %	24 %

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm
Dielectric Constant	2.9 <br>@Frequency 100 Hz	2.9 <br>@Frequency 100 Hz
	2.9 <br>@Frequency 1e+6 Hz	2.9 <br>@Frequency 1e+6 Hz
Dielectric Strength	35.0 kV/mm	889 kV/in
Dissipation Factor	0.0014 <br>@Frequency 100 Hz	0.0014 <br>@Frequency 100 Hz
	0.010 <br>@Frequency 1e+6 Hz	0.010 <br>@Frequency 1e+6 Hz
Comparative Tracking Index	600 V	600 V