- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 162 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 162 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | ASTM D648 |
| RheTech Products P100-00 Polypropylene, Natural Applications: Automotive componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | ASTM D648 |
| RheTech Products P102-00 Polypropylene, Black Applications: Consumer goodsIP structural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® FR23 ABS Flame retardant ABS (non-PBBE additives). Good properties/toughness. Excellent moldability. UL94 V-0 rated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C @Thickness 3.18 mm |
162 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Dry Blend E6001 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS (Asia Pacific) LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Faradex DX07304 PC (Asia Pacific) CF filled grade with EMI shieldingThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Faradex DX07304 PC (Asia Pacific) CF filled grade with EMI shieldingThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 300TE BK602 Acetal Homopolymer
(Unverified Data**) Delrin® 300TE BK602 is a medium-high viscosity toughened acetal homopolymer for injection molding with extremely low VOC emissions.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 17% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C @Thickness 6.40 mm |
162 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa FRHIPSV-0 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6mm, V-0 @ 3.2mmExcellent balance propertiesHigh mechanical strengthGood heat stabilityColor tailor-made for clientApplications:Injection moldingGas assistant moldingTV or aud.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-2 |
| Kureha KF Polymer 1300 PVDF Homopolymer KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Hostacomâ„¢ GP622 Polypropylene Homopolymer Description: Hostacomâ„¢ GP622 high melt flow, 2,900 MPa flexural modulus, 20% talc-filled polypropylene homopolymer is designed for high stiffness and excellent processability in thin-walled par.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | ASTM D648 |
| Spartech SP-9070 ABS/PVC Flame Retardant Sheet Description: Flame Retardant SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-1/-2 |
| Styrolution Polystyrol 143 E GR 2 PS Description: Polystyrol 143 E is a medium strength, easy flowing general purpose grade, suitable for blending with impact modified Polystyrol, Styrolux and coextruded gloss layers.Applications: In b.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXALEN PPH335T20 Polypropylene Homopolymer, 20% Talc Filled SAXALEN PPH335T20 is a 20% mineral filled Polypropylene - Homopolymer intended for injection molding with very good flow properties and higher stiffness by low warpage and good surface appearance.In.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-2 |
| Borealis Daploy™ WB260HMS Polypropylene Daploy™ WB260HMS is a propylene-based, structurally isomeric polymer. Applications: cushioning and protective packaging, door liners, lightweight packaging trays, beakers and containers, microwave.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-1, 2 |
| Polyplastics Duracon® SF-15 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Eastman Tenite 360E4861316 Cellulose Acetate Propionate, Clear, Trsp Applications:ProfilesProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Propionate 384A4000016 Clear, Trsp Cellulose Acetate Propionate Plasticizer 16%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Diamond Polymers ABS VP-11 SHF Description: High Flow, Flame Retardant ABSInformation provided by Diamond Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Eurostar Staramide R1000HI620 PA66, Impact Modified, Injection Molded Staramide R1000HI620 is an Impact Modified Polyamide 66 Injection Molding Resin (also known as R1000HI010)Information provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | ASTM D648 |
| Colorite Polymers 2018 Rigid PVC Description: Colorite Polymers offers a wide range of rigid vinyl compounds for extrusion and injection molding applications for the medical industry. These compounds can be formulated for the produ.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | ASTM D-648 |
| Axiall 7140 Rigid PVC, Extrusion & Molding Georgia Gulf 7140 is a special purpose rigid PVC compound designed for applications requiring the following properties: WeatherabilityGlossImpact Strength & ToughnessFlame RetardantChemical Resista.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0334W30L1 Wollastonite Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-2/AF |
| Addiplast Addilene J 520 M40 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75 |
| BASF Ultramid® NBX-0025 NF2001 PA66 (Dry) Ultramid NBX-0025 NF2001 is a specialty, unfilled PA6/6. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | ASTM D-648 |
| Axiall 8268 Rigid PVC, Extrusion Georgia Gulf 8268 is a rigid PVC pellet compound suited for applications where transparency is important. It is widely used for clear profiles such as furniture trim, shower door and protected jalo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Butyrate 465A3720010 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 10%. Weight loss on heating = 0.9% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F | ASTM E540 |
| Spartech APET SP4110 Copolyester Sheet Description: Copolyester SheetInformation provided by Spartech. |
|||