Sax Polymers SAXALEN PPH335T20 Polypropylene Homopolymer, 20% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXALEN PPH335T20 Polypropylene Homopolymer, 20% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXALEN PPH335T20 is a 20% mineral filled Polypropylene - Homopolymer intended for injection molding with very good flow properties and higher stiffness by low warpage and good surface appearance.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 20 % | 20 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 42.0 MPa | 6090 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 40.0 kJ/m² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 1.90 J/cm² @Temperature -30.0 °C |
9.04 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 103 °C | 217 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9955H TPE, ABS/PC Overmold
- Total 819E Polystyrene (discontinued **)
- SCG Chemicals EL-Proâ„¢ P702J Polypropylene Injection Molding
- A. Schulman POLYTROPE™ TPP 518 Injection Grade Olefinic Thermoplastic Elastomer
- Borealis Xmod™ K65G2 20% Glass Fiber Reinforced Polypropylene Compound
- Covestro Bayfit® SA Polyurethane Sound Absorbing Foam, High-Resilience, Higher density
- Alliance Polymers Viprene™ G40D-22U-NAT Thermoplastic Vulcanizate Elastomer
- Beijing Evergrow Resources UHF-F150 UHMW PE Fiber
- ATI Allegheny Ludlum Type 310L Stainless Steel
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N339 Filler
Copyright © lookpolymers.com All Rights Reserved