Aclo Accutech Polypropylene Homopolymer HP0334W30L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334W30L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 77 | 77 | ASTM D785 |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Elongation at Break | 18 % | 18 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ASTM D638 |
| Flexural Strength | 36.0 MPa | 5220 psi | ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 |
| Izod Impact, Notched | 0.432 J/cm | 0.810 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F |
Users viewing this material also viewed the following:
- H.C. Starck Amperit® 512.059 Agglomerated Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
- Teknor Apex Monprene® MP-1702A Thermoplastic Elastomer
- SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6 (Asia Pacific)
- Master Bond EP21TDC-4ND Two component, highly flexibilized epoxy for bonding, sealing and coating
- A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer
- DuPont™ Nomex® 410 Paper, 15 mil Nominal Thickness
- Dow FLEXOMER™ DFDB-9042 NT Very Low Density Polyethylene (VLDPE) Resin
- Eurostar Starglas FX05032 PE
- COI Ceramics Nicalon™ HI Type S SiC Ceramic Fiber
- Covestro Makrolon® LQ2687 Polycarbonate
Copyright © lookpolymers.com All Rights Reserved