Kureha KF Polymer 1300 PVDF Homopolymer

Category	Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer	Kureha
Trade Name	KF Polymer
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Kureha KF Polymer 1300 PVDF Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF polymer is being used in applications where heat resistance, anticorrosion, and weather-resistance are important.Typical Applications:Chemical valves, Pump part, & FittingsBinder for lithium ion batteriesHollow fiber for filtration of city water and sewageFilm & SheetInformation provided by Kureha.

Physical Properties	Metric	English	Comments
Density	1.77 - 1.79 g/cc	0.0639 - 0.0647 lb/inÂ³	ASTM D792
Viscosity	5000 cP @Shear Rate 50.0 1/s, Temperature 240 Â°C	5000 cP @Shear Rate 50.0 1/s, Temperature 464 Â°F	Melt; ASTM D3835
Viscosity Test	1.3 cmÂ³/g @Temperature 30.0 Â°C	1.3 cmÂ³/g @Temperature 86.0 Â°F	Inherent Viscosity in DMF Solution
Melt Flow	0.60 - 0.90 g/10 min @Load 5.00 kg, Temperature 230 Â°C	0.60 - 0.90 g/10 min @Load 11.0 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	67.0 MPa	9720 psi	ISO 527-2
Elongation at Break	25 %	25 %	ISO 527-2
Tensile Modulus	2.58 GPa	374 ksi	ISO 527-2

Thermal Properties	Metric	English	Comments
Melting Point	173 Â°C	343 Â°F	ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi)	72.0 Â°C	162 Â°F	ISO 75-2
Flammability, UL94	V-0 @Thickness 1.47 mm	V-0 @Thickness 0.0579 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1e+15 - 1e+16 ohm-cm	1e+15 - 1e+16 ohm-cm	ASTM D257