SABIC Innovative Plastics Cycolac® FR23 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® FR23 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant ABS (non-PBBE additives). Good properties/toughness. Excellent moldability. UL94 V-0 rated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Viscosity | 310000 cP | 310000 cP | Melt Viscosity, 200°C, 1000 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 9.0 g/10 min @Load 5.00 kg, Temperature 220 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 428 °F |
ISO 1133 | |
| Melt Index of Compound | 37 g/10 min @Load 10.0 kg, Temperature 220 °C |
37 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 11 % | 11 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.72 GPa | 395 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 41.0 J @Temperature 23.0 °C |
30.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 2.31 mm |
V-0 @Thickness 0.0909 in |
UL 94 |
| 5VB @Thickness 2.48 mm |
5VB @Thickness 0.0976 in |
UL 94 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 25 FRG 5 Polyamide 66, 25% Glass Fiber, Halogen Free Flame Retardant
- SABIC Innovative Plastics Lexan® FL910 PC
- Covestro Petlon® 4630 Semi-Crystalline PET, 30% Glass Fiber (discontinued **)
- Monmouth Rubber & Plastics Durafoamâ„¢ DK2121 NEO/EPDM Polymeric Blend
- Samsung Cheil Industries Starex® SF-100H Expandable Polystyrene (EPS) FR
- A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Braskem TI2900C High Crystallinity Copolymer Polypropylene
- Arlon EP2 Enhanced Polyimide Laminate and Prepreg
- BASF Ultrason S 2010 G4 20% Glass Filled PSU
Copyright © lookpolymers.com All Rights Reserved