- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 147 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 147 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP EIP12030F Polypropylene/EPDM, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Eastman Eastar GN005 Copolyester, Natural
(discontinued **) Eastar GN005 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN005 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 |
| Eastman 9921P PET Injection Molded
(discontinued **) Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Eastman EASTALLOY Polymer DA003-8999K, Clear Alloy
(discontinued **) Properties below based on a film thickness of 250 microns. CO2 Permeability is 49 cm3·mm/m2·24h·atm per ASTM D 1434.Product Description: EASTALLOY DA003-8999K Polymer is a clear copolyester/pol.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-2 |
| Polycasa COPOL PETG QUINN COPOL has good optical properties, brilliant surface, easy to vacuum form without pre-drying, low water absorption, very good chemical resistance, and high impact properties.Bus shelters (UV-v.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP EIP12030RF Polypropylene/EPDM, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | Unannealed; ISO 75-2/A |
| Ravago Manufacturing Americas Hylon® N1000STHL HF Nylon 6/6
(discontinued **) Available in North America Additive: Heat Stabilizer and LubricantFeatures: Lubricated, Heat Stabilized, High Flow and Ultra High ToughnessRoHS CompliantAuto Specifications: DELPHI DCM 4849 Color: B.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Hostacomâ„¢ TRC704D Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ TRC704D medium high melt flow, 1,500 MPa flexural modulus, UV-stabilized thermoplastic elastomeric olefin (TEO) resin has an excellent combination of properties and proce.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 LNP* LUBRICOMP* IL004 is a compound based on Nylon 6/12 resin containing 20% PTFE. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP VN001 Super Tough Nylon LNP* LUBRICOMP* VN001 is a compound based on Super Tough Nylon containing 2% MOS2. Added feature of th is grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY KX01002 Acetal Copolymer (Europe-Africa-Middle East) LNP* Stat-Loy* KX01002 is a compound based on Acetal Copolymer resin containing Antistat. Added features include: Permanent Anti-Static. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY KX95702 Acetal LNP STAT-LOY* KX95702 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-2 |
| Borealis PS65T20 Polypropylene Compound, Mineral Filled PS65T20 is a 20% mineral filled polypropylene compound intended for injection and back injection molding. This material has excellent balanced mechanical properties and high melt flow rate. Applic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene DescriptionPolyfort® FPP 2661 is a injection molding grade mineral fortified impact enhanced polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Eastman Eastar DN114 Copolyester, Natural Applications:LightingProduct Description: Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage. DN1.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Eastman Eastman 1223 Copolyester Applications:Blown filmCredit cardsDebit cardsDeodorant packagingElectronic packagingFabricated boxesFlexible packagingFood packagingFurniture/Furniture trimGaming cardsGift cardsIdentification card.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Eastman GSP01 Copolyester for Film and Sheet Extrusion Applications:Consumer e-packaging trayElectronic packagingElectrostatic dissipative trayProduct Description: GSP01 is a clear, amorphous material. Because of its clarity, toughness and good melt s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Butyrate 575E3720010 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Propionate 307A2R30013 Natural, Trsp Cellulose Acetate Propionate Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | ISO 75-2/A |
| ExxonMobil Exxtral™ HMU 234 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin, black colored, with high stiffness, high heat stabilization, low emissions and low odor for automotive HVAC and under-the-hood applic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 100STE NC010 Acetal (POM)
(Unverified Data**) Super Toughened High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 100STE NC010 (formerly DE20590) is a high-viscosity super-toughened acetal homopolymer with very low VOC emissions. P.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-2 |
| Denka CL-430 Transparent Resin Polymer (MABS) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starpylen MH0200A HDPE, Injection Molding Starpylen MH0200A is a High Density Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® ST801 NC010A Nylon 66
(Unverified Data**) Super Toughened Polyamide 6 Zytel ST801 is an unreinforced super tough polyamide 66 for injection molding and extrusion. It offers outstanding break resistance over a wide temperature and humidity r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | |
| Arkema Group Nakan® RRS 401 L PVC, Rigid Injection Grade NAKAN RRS 401 L is a rigid polyvinyl chloride compound developed for injection molding of waste water fittings.ISO data provided by the manufacturer, Arkema. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Braskem CP 401 HC Injection Molding Polypropylene Description: CP 401HC is a medium melt flow rate heterophasic copolymer, specially designed to achieve high stiffness/impact strength balance. This product offers good surface appearance and process.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.9 °C | 147 °F | ASTM D648 |
| RheTech Products CC30P100-00 30% Calcium Carbonate Reinforced Polypropylene, Natural Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Copyright © lookpolymers.com All Rights Reserved