SABIC Innovative Plastics LNP STAT-LOY KX95702 Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY KX95702 Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-LOY* KX95702 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption | 4.05 % | 4.05 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0174 cm/cm @Time 86400 sec |
0.0174 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm @Time 86400 sec |
0.018 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0183 cm/cm @Time 86400 sec |
0.0183 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
| 31.0 MPa | 4500 psi | ISO 527 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
| 41.0 MPa | 5950 psi | ISO 527 | |
| Elongation at Break | 52.4 % | 52.4 % | ISO 527 |
| 75.5 % | 75.5 % | ASTM D638 | |
| Elongation at Yield | 14.6 % | 14.6 % | ISO 527 |
| 18.1 % | 18.1 % | ASTM D638 | |
| Tensile Modulus | 1.11 GPa | 161 ksi | 1 mm/min; ISO 527 |
| 1.50 GPa | 218 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
| 46.0 MPa | 6670 psi | ASTM D790 | |
| Flexural Modulus | 1.35 GPa | 196 ksi | ISO 178 |
| 1.38 GPa | 200 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 22.0 J | 16.2 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 16.0 J | 11.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 124 µm/m-°C @Temperature -40.0 - 40.0 °C |
68.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 124 µm/m-°C @Temperature -40.0 - 40.0 °C |
68.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 139 µm/m-°C @Temperature -40.0 - 40.0 °C |
77.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 139 µm/m-°C @Temperature -40.0 - 40.0 °C |
77.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 78.0 °C @Thickness 3.20 mm |
172 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO-LOCK SERIES 13-OR Anaerobic Thread Locking Compound
- SABIC Innovative Plastics Lexan® EXL1112T PC Copolymer
- Gwent Electronic Materials P2121112P10 Ammonia Plasma Modified Multiwalled Carbon Nanotubes
- Techmer ES HiFill® PA4/6 CF30 30% Carbon Filled (Dry)
- Shin-Etsu Silicones KEG-2000-30A/B Elastomer
- ChevronTexaco Delo® ESI® Trans Fluid
- ConocoPhillips Conoco® El Mar® 2000 Oil SAE Grade 40
- BASF Heligoen® Blue 6989 F Color Additive
- 3M Scotch® 353 High Performance Box Sealing Tape
- Bulk Molding Compounds tetra-DUR N 4203 Bulk Molding Compound
Copyright © lookpolymers.com All Rights Reserved