- Polykemi AB POLYfill PP EIP12030RF Polypropylene/EPDM, Mineral Reinforced
Polykemi AB POLYfill PP EIP12030RF Polypropylene/EPDM, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP EIP12030RF Polypropylene/EPDM, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | With Flow; ISO 2577 |
| 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 26.0 MPa | <= 3770 psi | ISO/R527 |
| Elongation at Break | 16 % | 16 % | ISO/R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 45.0 MPa | <= 6530 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa @Temperature 23.0 °C |
363 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 2.40 J/cm² @Temperature -20.0 °C |
11.4 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 - 75.0 µm/m-°C | 30.6 - 41.7 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 75.0 °C @Load 5.001 kg |
167 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 145 °C @Load 1.00 kg |
293 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Scratch Resistance, 10N (dL) | 6.9 | 10N Fine Structure; ISO 1518/D65 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Q70W Polyurethane Rubber
- PolyOne Geon™ HTX L1502 Polyvinyl Chloride Alloy (PVC Alloy)
- Kazanorgsintez E-11 Petroleum Resin
- International Mold Steel Daido DRM1 Matrix High-Speed Steel
- Henkel Hysol AL 2000 Primer
- SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66 (Asia Pacific)
- Teknor Apex Sinpolene TPP2010 Polypropylene
- Weartech International WT-800 Cobalt Hardfacing & Wear Resistant Alloy
- A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR Plasthall 7050 Plasticizer
Copyright © lookpolymers.com All Rights Reserved