SABIC Innovative Plastics LNP STAT-LOY KX01002 Acetal Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-LOY KX01002 Acetal Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-Loy* KX01002 is a compound based on Acetal Copolymer resin containing Antistat. Added features include: Permanent Anti-Static.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
Water Absorption 4.8 %

@Time 86400 sec
 4.8 %

@Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.028 cm/cm
0.028 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 43.0 MPa
6240 psi
5 mm/min; ISO 527
Elongation at Yield 15.8 %
15.8 %
5 mm/min; ISO 527
Tensile Modulus 1.60 GPa
232 ksi
1 mm/min; ISO 527
Flexural Yield Strength 52.0 MPa
7540 psi
2 mm/min; ISO 178
Flexural Modulus 1.60 GPa
232 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 - 1.00e+12 ohm-cm
1.00e+10 - 1.00e+12 ohm-cm
ASTM D257
Surface Resistance 1.00e+10 - 1.00e+12 ohm
1.00e+10 - 1.00e+12 ohm
ASTM D257