- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 126 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 126 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 6005 PC/ABS-Blend Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 - 104 °C | 126 - 219 °F | Average value: 64.8 °C Grade Count:18 |
| Overview of materials for Polypropylene, Fiber Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Fiber Grade". Each property range of values reported is minimum and maximum values of app.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Butyrate 513E3720008 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Pro-faxâ„¢ SG899 Polypropylene Copolymer Description: Pro-faxâ„¢ SG899 high flow, high impact polypropylene copolymer resin is tailored for use in automotive interior head impact applications. This resin is designed to be run in convent.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-9000 Polypropylene Block-Copolymer INNOPOL® CS 2-9000 is a polypropylene block-copolymer based compound. This grade is available in nature and custom colored form.INNOPOL® CS 2-9000 is developed for producing injection molded a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ASTM D648 |
| A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75 B |
| Borealis Borsoft™ SF203CF Soft Polypropylene Copolymer for Extrusion Coating Borsoft SF203CF is a new statistic-heterophasic propylene-ethylene copolymer suitable for coating applications. Its polymer structure permits perfect adhesion to certain products. According to the.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-2 |
| Borealis Daplen™ EG250AI Polypropylene TPO Compound Daplen™ EG250AI is a 20% mineral reinforced impact modified polypropylene compound suitable for injection molding. This material has an excellent balance between impact strength and stiffness, giv.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75 |
| Unipetrol PP MONSTEN® MA 612 Polypropylene Impact Copolymer Made for injection molding applications. Antistatic stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 75-2 |
| Total PPC 7650 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 7650 is a nucleated and antistatic heterophasic copolymer. PPC 7642 is characterized by a medium fluidity offering a combination of ease of processing and excellent impact propert.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 752 |
| Total PPC 7652 Polypropylene, Heterophasic Copolymer, Injection Molding Polypropylene PPC 7652 is a nucleated and antistatic heterophasic copolymer with a Melt Flow index of 16 g/10 min.Polypropylene PPC 7652 is a medium flow grade intended for a wide range of injection.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 75-2 |
| Total PPH 9099 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9099 is a very narrow molecular weight distribution homopolymer polypropylene, with anti gas-fading stabilization. ApplicationATOFINA Polypropylene PPH 9099 is intended for.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 752 |
| Total PPM H250 Polypropylene, Homopolymer Medical Grade Polypropylene PPM H250 is a narrow molecular weight distribution homopolymer with a Melt Flow Index of 25 g/10 min recommended for the manufacture of medical packaging and medical devices, to the ex.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 75-2 |
| Total PPC 3640 Polypropylene, Heterophasic Copolymer ATOFINA Polypropylene PPC 3640 is a nucleated heterophasic copolymer. PPC 3640 is characterized by improved stiffness, creep resistance and high impact resistance.ApplicationPPC 3640 has been devel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ASTM D648 |
| A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ISO 75-2/A |
| ExxonMobil Exxtral™ CNU 015 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with good stiffness/toughness balance, low odor and emissions, designed for automotive interior applications. Availability: Africa & M.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ISO 75-2/A |
| ExxonMobil PP1014H1 Polypropylene Homopolymer Product Description: A homopolymer resin that meets certified requirements for use in Medical and Pharmaceutical applications.Availability: Europe and North America Features:Autoclave SterilizableE.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ISO 75-2/A |
| ExxonMobil PP1063L1 Polypropylene Homopolymer Product Description: A homopolymer resin designed for general use. It is suitable for masterbatch carrier and other compounding applications and for the molding of caps, cups, containers and other .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ISO 75-2/Bf |
| ExxonMobil PP7033N Impact Copolymer Product Description: A high crystallinity, high stiffness, high impact copolymer resin designed for injection molding applications requiring medium melt flow rate, good processing characteristics a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | DAM; ASTM D648 |
| DuPont Performance Polymers Zytel® ST811HS NC010 Nylon 6
(Unverified Data**) Zytel® ST811HS is a flexible, heat stabilized Super Tough polyamide 6 resin developed for extrusion and injection molding applications such as cable and rope jacketing, hose inner cores and fastene.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0334C10L1 Calcium Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Braskem CP 144 Coating Polypropylene Information provided by Braskem |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | |
| 3M Dyneon™ PVDF 11010/0000 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 11010/0000 is a copolymer of VF2 and HFP (hexafluoropropylene). Recommended for flared tubing, it combines excellent chemical resistance, and dimensional stability with a moderate.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 752 |
| Total PPC 3120 MU5 Polypropylene, Heterophasic Copolymer, Automotive Polypropylene PPC 3120 MU5 is a heterophasic copolymer with a Melt Flow index of 15 g/10 min. Polypropylene PPC 3120 MU5 is a high impact copolymer formulated to give good UV resistance.Polypropyle.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 - 86.0 °C | 126 - 187 °F | Average value: 70.3 °C Grade Count:92 |
| Overview of materials for Cellulose Acetate Butyrate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Butyrate, Molded". Each property range of values reported is minimum and maximum value.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Hifax™ HSBMF248 Thermoplastic Polyolefin Elastomer Description: Hifax™ HSBMF248 high melt flow, 1,400 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of flow, rigidity, low t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Stat-kon MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB.. |
|||